Recovery of Platinum Group Metals from Spent Automotive Catalyst

S. Dragulovic,M. Dimitrijević,A. Kostov,S. Jakovljevic

Abstract:A special treatment of platinum group metals (PGMs) leaching from spent automotive catalyst is shown in this paper. Leaching of crushing and grinding automotive catalyst scrap in hydrochloric acid with defined concentration, added nitric acid as oxidant, produced chloride solution of the platinum group metals, while catalyst substrate (Al 2 O 3) remained indissoluble. Cementation of the leached platinum group metals from solution was made by powered aluminum with suitable pH values. The precipitate obtained by cementation with Al-powder is mixture of the platinum group metals and surplus aluminum. The surplus aluminum can be removed by selected resolving with hydrochloric acid. The mixture of platinum group metals (Pt, Pd, and Rh) is obtained by this treatment. Separation between platinum group metals was done by well-known chemical processes. 1. INTRODUCTION Automotive catalysts have been extensively used for reducing the amount of unburned hydrocarbons (HC), carbon monoxide (CO), and nitrogen oxides (NO x) from the exhaust gas emitted by automobiles. Platinum group metals (PGMs) have been used as catalytic agents because of their heat resistance and special catalytic activity. The content of total PGMs in automotive catalyst is about 0.5 to 2.0 g per kilogram. Autocatalyst essentially comprise a refractory oxide carrier on which two or more precious metals are dispersed in very low concentration. The worldwide demand of PGMs used for autocatalysts has increased with rapid motorization and the enforcement of stringent regulations for exhaust gas. In 2001, 37% of the worldwide demand for platinum, 72% of palladium and 85% of rhodium was for their use as automotive catalysts. In the year 2003, the overall demand of platinum was about 200 metric tons; 5% had to be met from stock in the last years because of lower primary and secondary production. Half of the produced platinum was used for catalysts in the automotive industry. From this, one third is covered by platinum out of secondary metallurgical processes [1,2]. Due to their scarcity and high price, the recovery of PGMs from spent automotive catalyst, generally called catalyst scrap, is a very important. The catalyst scrap generally consists of the surface layer with a high degree of porosity and the catalyst substrate (such as SiO 2 , Al 2 O 3 and CeO 2) with honeycomb structure. Ceramic materials were chosen for the initial monolith and they still dominate market. The preferred materials is called cordierite (synthetic cordierite has a composition approximating 2MgO, …

Chemistry,Engineering,Materials Science