Abstract:Fe3O4@SiO2 particles were synthesized by a solvothermal method and a classical stOber method. Superparamagnetic Fe3O4 was the core, and a sol-gel coating of SiO2 was the shell. After the SiO2 surface was modified with amino groups, benzaldehyde was conjugated to the particles by a Schiff base reaction. The Fe3O4@SiO2 particles were emulsified in paraffin/water as a solid emulsifier to obtain an oil-in-water Pickering emulsion. After cooling the paraffin, the particles were fixed on the surface of the emulsion droplets. The particles were etched in ammonium fluoride aqueous solution, and Janus particles with different structures could be obtained by adjusting the etching time. Via the in situ growth of metal Pt or Ag nanoparticles, superparamagnetic Fe3O4@SiO2-Pt or Fe3O4@SiO2-Ag Janus particles were obtained. The movement of Fe3O4@SiO2-Pt Janus particles was observed due to the catalytic decomposition of hydrogen peroxide aqueous solution. It was found that in the short term, there was a linear motion, while in the long term, the motion direction and trajectory were random. Fe3O4@SiO2-Ag Janus particles were used as magnetic solid surfactants to stabilize the emulsions and catalyze the nitro reduction. About 60% of the surficial area of the Janus particles was modified by phenyl groups, while the remaining 40% was covered with Ag nanoparticles. Under the premise of maintaining the Janus balance, the whole particle became more hydrophobic, which was conducive to the formation of the water-in-oil emulsion. In addition, the Ag side of the Janus particles was towards the aqueous phase, and the opposite hydrophobic side was towards the oil phase. The Janus particles possessed a fixed orientation assembly at the oil-water interface. The assemble membrane possessed Janus characteristics, and it facilitated the stable dispersion of the emulsion and the catalysis. The method has the advantages of a simple principle, capability for mass production, universality and versatility. It is expected that Janus particles will be used to more precisely regulate the zoning with different functional substances.

Amphiphilic Titania Janus Nanoparticles Containing Ionic Groups prepared in Oil-Water Pickering Emulsion

Janus Nanoparticles with Tunable Amphiphilicity for Stabilizing Pickering-Emulsion Droplets via Assembly Behavior at Oil-Water Interfaces.

Preparation of Polymer Hollow Microspheres Covered by Polymer Solid Particles Via Two Polymerization Steps

Efficient Fabrication of Janus Particles with Active Groups and Application in Emulsion Stabilization and Interfacial Catalysis

Fabrication of Amphiphilic Porous PDVB-PAA Janus Nanoparticles: Formation Mechanism, Simultaneous Loading and Regulated Release of Hydrophobic and Hydrophilic Cargos

Preparation and properties of Janus nanoparticles at pickering emulsion interface

Effect of an Anionic Monomer on the Pickering Emulsion Polymerization Stabilized by Titania Hydrosol

Tailoring Surface Structure of Polymer Nanospheres in Pickering Emulsion Polymerization.

Janus Nanoparticles by Interfacial Engineering

Amphiphilic Janus Microspheres Prepared by Caged Photoactivatable Alkoxysilane

Readily Available Titania Nanostructuring Routines Based on Mobility and Polarity Controlled Phase Separation of an Amphiphilic Diblock Copolymer.

Multifunctional Fe3O4@SiO2 Janus Particles

Preparation, Morphology, Wettability And Mechanism Of Nanometer Titania Film

Modification of Titania Particles Coated with Polystyrene Particles Film

Hybrid Titania Microspheres of Novel Superstructures Templated by Block Copolymers

Janus-like Pickering emulsions and their controllable coalescence.

Spatial Isolation of Carbon and Silica in a Single Janus Mesoporous Nanoparticle with Tunable Amphiphilicity

Emulsion Interfacial Synthesis of Polymer/Inorganic Janus Particles

Polymeric Janus Particles with Hierarchical Structures

Dumbbell‐Shaped Bi‐component Mesoporous Janus Solid Nanoparticles for Biphasic Interface Catalysis

Janus non-spherical colloids by asymmetric wet-etching.