Abstract:Considerable quantities of Nd-Fe-B magnet wastes are produced every year worldwide. Some Nd-Fe-B magnet wastes in the bulk form, produced during manufacturing, have low coercivity and cannot meet the requirements for applications. Finding an effective way to reuse those wastes by improving the coercivity, without powdering or reproducing process, becomes very important for saving energy and raw materials in manufacture. In this work, the grain boundary diffusion process is carried out on waste Nd-Fe-B sintered magnets by using Pr70Cu30 as a diffusion medium. The effects of diffusion temperature, diffusion time, and annealing time on the magnetic properties of the magnets are investigated. It is found that the coercivity increases when the diffusion temperature increases from 500 to 800 degrees C, the diffusion time increases from 1 to 3 h, or the annealing time increases from 1 to 3 h. By comparing the diffused sample with the simply heat treated sample, we find that the coercivity enhancement by grain boundary diffusion process indeed results from the infiltration of Pr and Cu elements. The coercivity of the magnet increases by 51.9%, from 7.88 kOe (1 Oe = 79.5775 A/m) to 11.97 kOe, after 4-hour diffusion at 800 degrees C followed by 3-hour annealing, with a negligible reduction of remanence B-r, achieving a 99.8% recovery of coercivity compared with the commercial N35 magnet. It is noted that 500 degrees C annealing for 3 h after 800 degrees C diffusion only slightly increases the coercivity by 4.6%, from 11.44 kOe to 11.97 kOe, which indicates that the annealing process after Pr-Cu grain boundary diffusion may be not indispensable. Based on the microstructure analysis, the diffusion of Pr and Cu is confirmed. However, the distributions of Pr and Cu are inhomogeneous within a range of tens of microns near the surface even though the diffusion has spread throughout the magnet. The structure of main phase grains separated by the continuous grain boundary phase is formed after the grain boundary diffusion process while the core-shell structure is not observed, which suggests that the modification of the grain boundary structure is the main reason for the coercivity improvement. Cu element plays an important role in forming continuous grain boundary phase. In addition, the electrochemical corrosion test shows that higher corrosion current is obtained in the diffused magnet than in the original magnet, though the corrosion potential is improved. The reduced corrosion resistance may be related to the increased RE-rich phase content and the formation of continuous grain boundary phase. The present work is of great importance for increasing the production yield of Nd-Fe-B magnets.

High-Coercivity Nanocrystalline Nd-Fe-B Powder Regenerated from Sludge via In-Situ Mechanochemical Approach

New strategy for the ultra-short process regeneration of sintered Nd-Fe-B sludge via purification-remixing incorporation

Nd-Fe-B: From sludge waste to powders via purification and modified Ca-reduction reaction process

A facile process to optimize performance of regenerated Nd-Fe-B sintered magnets: Chemo-selective dissolution washing

An efficient process for preparing regenerated magnets by dynamic recovery of Nd-Fe-B sintered magnet sludge

Preparation of (Nd, Ce)-Fe-B Regenerated Magnets by In-Situ Restoration of Grain Boundary Structure Using Nascent Nd-Fe-B Powder

Mass production of regenerated sintered NdFeB magnets with improved magnetic properties compared to original magnets

Effect of diffusion medium on the regeneration of Nd-Fe-B magnet sludge by CaH 2 reduction diffusion method

Synthesis of hard magnetic NdFeB composite particles by recycling the waste using microwave assisted auto-combustion and reduction method

A cleaner and sustainable method for recovering rare earth and cobalt from NdFeB leaching residues

In situ anodic leaching of Nd-Fe-B sludge with fast leaching kinetics for selective recovery of rare-earth elements

Rapid coercivity increment of Nd–Fe–B sintered magnets by Dy69Ni31 grain boundary restructuring

Towards the Improvement of the Short‐Loop Recycling of Dy‐Rich Nd‐Fe‐B Permanent Magnets: Experimental and Numerical Approaches

Preparation of Highly Textured Hydrogenation-Disproportionation-desorption-recombination Powders for Nd-Fe-B Sintered Magnets

Fabrication of Low-Cost Nd–Fe–B Sintered Magnets Reusing Ultrafine Powders

Nd-Fe-B Sintered Magnets with Low Rare Earth Content Fabricated Via Dy71.5Fe28.5 Grain Boundary Restructuring

Restoring and enhancing the coercivity of waste sintered (Nd,Ce,Gd)FeB magnets by direct Pr–Tb–Cu grain boundary diffusion

Improved room-temperature-selectivity between Nd and Fe in Nd recovery from Nd-Fe-B magnet

Enhanced Coercivity of Nd-Ce-Fe-B Sintered Magnets by Adding (nd, Pr)-H Powders

Coercivity enhancement of waste Nd-Fe-B magnets by Pr70Cu30 grain boundary diffusion process

Synergistic grain boundary modification and magnetic hardening for coercivity enhancement in Nd-Ce-Fe-B sintered magnets with Dy Cu addition