Abstract:The conductive nano-Al/polyaniline composites were prepared by the milling method in the solid state. Here, aluminum nanostructures were prepared in two different mechanical methods, wire drawing and wire milling in the presence of lubricant oil. The effects of the preparation methods on the structures and morphologies of aluminum nanostructures were investigated by XRD and FESEM. The results show that the shape and size of aluminum nanoparticles in the preparation by the wire drawing method are significantly different than the wire milling method. The aluminum nanostructures were prepared by milling method have flake-like nanosheets while the wire drawing method leads to the formation of spherical ultrafine nanoparticles, which particles size are in the range of 30–60 nm. Then, polyaniline was produced using a solid-state polymerization process by the chemical reaction between aniline hydrochloride and potassium peroxydisulfate. Finally, nano-Al/polyaniline composites were prepared by mechanical milling at room temperature. The quantitative analysis was carried out with the materials analysis using diffraction (MAUD) method and weight fraction for aluminum and PANI were calculated 6.66% and 93.34%, respectively. Electrical conductivity measurements show the conductivity (1.2 × 10 −2 S cm −1 at 25 °C) for polyaniline emeraldine salt and (1.02 × 10 −3 S cm −1 at 25 °C) in nanocomposite respectively. The results show that by adding aluminum nanoparticles to the polymer the conductivity of nanocomposite (Al/PANI-ES) is lower than that for pure (PANI-ES). Thermogravimetry and differential thermal analysis curves show pure (PANI-ES) and nanocomposite (Al/PANI-ES) have a similar thermal degradation process. The total weight loss in TG curve of pure PANI-ES, in the temperature range 45–800 °C is 46.28% but, total weight loss observed in nanocomposite is 38.67%. Therefore, nanocomposite has higher thermal stability than that of the pure PANI-ES.

Comparison of semi-doped PANI/DBSA complex achieved by thermal doping and roll-mill process: A new perspective for application

Preparation of Polyaniline Doped with Acid and Polymer Using Electrochemical Deposition

Development of Electrically Conductive Thermosetting Resin Composites through Optimizing the Thermal Doping of Polyaniline and Radical Polymerization Temperature

Recent Progress in Design of Conductive Polymers to Improve the Thermoelectric Performance

Probing the influence of ZnFe2O4 doping on the optical and dielectric characteristics of PMMA/PANi

Electrically Conductive PANI-DBSA/Co-PAN Composite Fibers Prepared by Wet Spinning

Prospective on Doping Engineering of Conductive Polymers for Enhanced Interfacial Properties

Conductive Polyaniline Doped with Dodecyl Benzene Sulfonic Acid: Synthesis, Characterization, and Antistatic Application

Enhancement of Electrical Properties of Ferroelectric Polymers by Polyaniline Nanofibers with Controllable Conductivities

Progress in preparation, processing and applications of polyaniline

Electrical and Structural Analysis of Conductive Polyaniline/polyacrylonitrile Composites

High-Dielectric PVP@PANI/PDMS Composites Fabricated via an Electric Field-Assisted Approach

Effect of polyaniline content and protonating dopants on electroconductive composites

Structural, thermal, optical characterizations of polyaniline/polymethyl methacrylate composite doped by titanium dioxide nanoparticles as an application in optoelectronic devices

Achieving Secondary Dispersion of Modified Nanoparticles by Hot-Stretching to Enhance Dielectric and Mechanical Properties of Polyarylene Ether Nitrile Composites

Conductive nano-Al/polyaniline composites prepared via mechanical milling

Design of a Low-Cost PMMA/PVAc/PANI Blended Polymers: Structural, Electrical and Dielectric Characteristics

Preparation of the PAn/PMMA Conductive Composite by In-Situ Emulsion Polymerization

Enhanced electrical and thermal properties of semi-conductive PANI-CNCs with surface modified CNCs

Molecular Dynamics Simulation Study on the Structural and Thermodynamic Analysis of Oxidized and Unoxidized Forms of Polyaniline

Greatly increased electrical conductivity of PBTTT-C14 thin film via controllable single precursor vapor phase infiltration