Influencing mechanisms of C content and aging treatment on intergranular corrosion sensitivity of 316 stainless steel weld metals

Shitong Wei,Langlang Zhao,shanping lu

DOI: https://doi.org/10.2139/ssrn.4835776

IF: 6.267

2024-06-09

Journal of Materials Research and Technology

Abstract:For analyzing the intergranular corrosion sensitivity of 316 stainless steel weld metals with different C contents, the intergranular corrosion behaviors of the weld metals under as-welded and different as-aged states were evaluated by both the H 2 SO 4 -CuSO 4 solution corrosion method and the double loop electrochemical potentiokinetic reactivation method, respectively. The results indicate that after long term aging treatment at 550 °C, the δ ferrite in high C weld metal has a higher transformation fraction than that in low C weld metal, which results in a higher intergranular corrosion sensitivity for high C weld metal. However, after the long term aging treatment at 600 °C, the δ ferrite in high C weld metal transforms completely in the early stage aging, and with increasing of the aging time, the desensitization process occurs in the Cr-poor region of high C weld metal, which improves the intergranular corrosion resistance, and results in a higher intergranular corrosion sensitivity for low C weld metal. Therefore, under the service environment of considering the intergranular corrosion performance of the weld metal, the welding material with the appropriate C content should be selected according to the service temperature.

materials science, multidisciplinary,metallurgy & metallurgical engineering