Abstract:Biomass-derived porous carbons have received an extensive importance as effective electrode materials owing to their abundance and low cost. The unique porous architectures and large specific surface areas of biomass are beneficial for manipulating the charge storage performance of assembled supercapacitor devices. Here, we demonstrate nitrogen and phosphorus self-doped hierarchical porous carbon (N/P-HPC) derived from yeast (Y) and phytic acid (PA) precursors via freeze-drying-assisted esterification reaction and pyrolysis treatment. The supercapacitive performance and charge storage capability of N/P-HPC were regulated by optimizing the Y/PA composition and controlling the carbonization temperature. Accordingly, the resultant N/P-HPC-Y:PA(2:1)-800 (fabricated with an optimized Y:PA ratio of 2:1 and carbonized at 800 °C) reveals a high specific surface area of 978 m2 g−1 and a large pore volume of 0.592 cm3 g−1. As an electrode material, N/P-HPC-Y:PA(2:1)-800 delivers a high specific capacitance of 432 F g−1 at a current density of 1 A g−1 and can sufficiently retain about 250 F g−1 at 20 A g−1 under a three-electrode cell configuration in 1.0 M H2SO4 electrolyte. Moreover, the as assembled symmetric supercapacitor device operated with the N/P-HPC-Y:PA(2:1)-800 as both positive and negative electrode material exhibits an energy density of 13.6 Wh kg−1 at a power density of 500 W kg−1. Even at a larger current density of 20 A g−1, the device maintains an energy density of 10.4 Wh kg−1 and a maximum power density of 10 kW kg−1. The constructed device displays a large capacitance retention of 93.3% after 10 000 charge/discharge times at a higher current density of 10 A g−1, manifesting the enhanced cycling stability.

Enhanced Energy Density for P-Doped Hierarchically Porous Carbon-Based Symmetric Supercapacitor with High Operation Potential in Aqueous H2SO4 Electrolyte

Improving the Pore-Ion Size Compatibility Between Poly(ionic Liquid)-Derived Carbons and High-Voltage Electrolytes for High Energy-Power Supercapacitors

Hydrangea-like N/O codoped porous carbons for high-energy supercapacitors

Hierarchical Porous Carbon Guided by Constructing Organic-Inorganic Interpenetrating Polymer Networks to Facilitate Performance of Zinc Hybrid Supercapacitors

Oxide-doped hierarchically porous carbon for high-performance supercapacitor

Cooking Carbon with Protic Salt: Nitrogen and Sulfur Self-Doped Porous Carbon Nanosheets for Supercapacitors

Phosphorus-doped 3D hierarchical porous carbon for high-performance supercapacitors: A balanced strategy for pore structure and chemical composition

Polytetrafluoroethylene-assisted removal of hard-template to prepare hierarchically porous carbon for high energy density supercapacitor with KI-additive electrolyte

Synthesis of hierarchically porous boron-doped carbon material with enhanced surface hydrophobicity and porosity for improved supercapacitor performance

Phosphorus-doped thick carbon electrode for high-energy density and long-life supercapacitors

Facile synthesis of N/P co-doped carbons with tailored hierarchically porous structures for supercapacitor applications

Hierarchical porous carbon sheets derived on a MgO template for high-performance supercapacitor applications

Nitrogen and Phosphorus Co-doped Porous Carbon for High-Performance Supercapacitors

Heteroatoms Doped Porous Carbon Derived from Waste Potato Peel for Supercapacitors

Toward High-Rate Supercapacitor: Preparation of Hierarchical Porous Carbon Binder-Free Electrode with Controllable Texture

Hierarchically Porous Carbon Derived from an Aqueous Curable Composition for Supercapacitors

Nature-inspired Self-Activation Method for the Controllable Synthesis of Highly Porous Carbons for High-Performance Supercapacitors

Organic salt-derived phosphorus-doped mesoporous carbon for high performance supercapacitors

3D hierarchical porous carbon matching ionic liquid with ultrahigh specific surface area and appropriate porous distribution for supercapacitors

Phosphorus-Mediated Local Charge Distribution of N-Configuration Adsorption Sites with Enhanced Zincophilicity and Hydrophilicity for High-Energy-Density Zn-Ion Hybrid Supercapacitors

Strategic N/P self-doped biomass-derived hierarchical porous carbon for regulating the supercapacitive performances