Abstract:Ferrites with spinel structure (FSS), especially FSS with doping, show excellent thermal stability and high infrared emissivity performance and can thus be used for improving radiation heat transfer in industrial flame furnaces. In this study, CuxCo1-xFe2O4 samples with varying CuO doping contents (0%, 12.5%, 25%, 37.5%, 50%, 62.5% and 75%) were prepared by a sintering process to study the mechanism of doping on the emissivity of FSS in the 8-14 mu m and 3-5 mu m wavebands to improve the preparation of FSS with excellent performance. The emissivity in the 8-14 mu m and 3-5 mu m bands was measured by an IR-2 dual-band emissivity measurement instrument. The results show that in the 8-14 mu m band, the samples have an obvious increase from 0.869 to 0.925 with CuO addition to 12.5% and a slight increase from 0.93 to 0.94 with further doping from 12.5% to 75%. For all the samples, the force constant for the octahedral position (KO) was calculated based on the data obtained from Fourier transform infrared (FT-IR) spectroscopy and XRD refinement. The result shows that the sample with smaller KO has higher emissivity in the 8-14 mu m band. While for the 3-5 mu m band, there is a minimum value (0.62) in the emissivity at a CuO doping content of 12.5%, with an increase in emissivity observed from 0.62 to 0.77 upon further doping from 12.5% to 75%. The band gap for the as-prepared FSS samples was measured by UV-visible absorption spectra, and it was found that the smaller the band gap is, the higher is the emissivity in the 3-5 mu m band, which indicates that a decreased band gap can increase the energy of electron absorption or emission during the electron transition process for FSS. Thus, the effect of K-0 and band gap on the emissivity in the middle and short waveband was identified in this study, which is of significance for the design and preparation of FSS materials with high emissivity in the middle and short wavebands. (C) 2019 Elsevier B.V. All rights reserved.

Enhanced near- and mid-infrared radiation property of MgCr2O4 by doping with Cu ions

Effects of Mg doping on structural and optoelectronic properties of p-type semiconductor CuCrO2 thin films

Enhancing thermal and dielectric properties of MgO–Al2O3–SiO2–B2O3 glass-ceramics through CuO doping

The Effect of Microstructure on the Middle and Short Waveband Emissivity of CuO-doped CuxCo1-xFe2O4 Spinel

Novel Cu2+-Fe3+ co-doped LaAlO3 ceramic with high infrared radiation performance

Preparation of infrared high radiation coatings from modified spinel NiFe2O4 and its energy saving applications

Broadband near-infrared emission in Cr3+-doped MgO-Al2O3-SiO2 dual-phase glass-ceramics for near-infrared spectroscopy applications

Crystallization and infrared radiation properties of iron ion doped cordierite glass-ceramics

Microstructure, Thermal Conductivity, and Temperature-Dependent Infrared Emissivity of Divalent Transition Metal Ions Doped A-Cordierite Ceramics

Microstructure, thermal conductivity, and temperature-dependent infrared emissivity of divalent transition metal ions doped α-cordierite ceramics

Effect of Ga3+ ion doping on emission thermal stability and efficiency of MgAl2O4:Cr3+ phosphor

Preparation, microstructure, and thermophysical properties of Cr3+-modified cordierite high emissivity ceramic for metal thermal protection

Simultaneous Absorption and Near‐Infrared Emission Enhancement of Cr3+ Ions in MgGa2O4 Spinel Oxide via Anionic F‐Substitution

MgCr2O4-Modified CuO/Cu2O for High-Temperature Thermochemical Energy Storage with High Redox Activity and Sintering Resistance

Greatly enhanced broadband near-infrared emission due to energy transfer from Cr<sup>3+</sup> to Ni<sup>2+</sup> in transparent magnesium aluminosilicate glass ceramics

Intense narrow band blue emission in CuCrO 2 delafossite by Ni 2 + -Mg 2 + dual cation doping

Greatly enhanced broadband near-infrared emission due to energy transfer from Cr 3+ to Ni 2+ in transparent magnesium aluminosilicate glass ceramics

Characterization of structure and properties of MgO-Al2O3-SiO2-B2O3-Cr2O3 glass-ceramics

Improved Energy Transfer in Mn-Doped Cs3Cu2I5 Microcrystals Induced by Localized Lattice Distortion

Effect of Ca2+/Cr3+doping ratio on the infrared radiation performance and Cr6+ formation in LaAlO3 ceramics

Ca2+‐Doped LaCrO3: A Novel Energy‐Saving Material with High Infrared Emissivity