Abstract:AlCrFeNiCu high-entropy alloy (HEA) coating was prepared on Zirconium (Zr) rod by high-speed laser cladding (HSLC) technique. The effect of different laser power and scanning speed on the forming quality of the coating was studied. When the specific energy density was in the range of 3.0–3.2 J/mm 2 , the AlCrFeNiCu HEA coating with good adhesion to the substrate, low dilution rate (small heat affected zone) and no cracks were obtained. The phase structure, microstructure, microhardness, corrosion resistance and high temperature oxidation resistance of the coating were tested and analyzed. The results show that the AlCrFeNiCu HEA coating is composed of 76.9 % BCC phase and 23.1 % FCC phase, in which the BCC phase is mainly composed of disordered BCC phase rich in Cr and Fe elements and ordered B2 phase rich in Al and Ni elements, and the FCC phase is rich in Cu elements. Due to the rapid cooling of HSLC, the coating structure gradually changes from columnar crystal to equiaxial crystal from bottom to top. The hardness of the coating is as high as 805 HV, which may be caused by the solution strengthening effect, lattice distortion effect and slow diffusion effect of HEA. In 3.5 % NaCl solution and 0.1 mol/L KOH solution, the self-corrosion current density of the coating is 4.209 × 10 −8 A/cm 2 and 4.331 × 10 −8 A/cm 2 , respectively. The passivation film on the surface of the coating is composed of a variety of oxides, and the oxygen vacancy density of the passivation film in the two solutions is 2.552 × 10 20 cm −3 and 5.794 × 10 20 cm −3 , with fewer pitting pits on the surface. The structural integrity of the coating can be maintained after 60 min oxidation at 1200 °C. The oxidation process follows the growth kinetics curve, and the surface oxides mainly comprise FeAl 2 O 4 , Al 2 O 3 and Cr 2 O 3 . AlCrFeNiCu HEA coating improves the corrosion resistance and high temperature oxidation resistance of the Zr-4 alloy.

Effects of tempering treatment on structural evolution and electrochemical properties of laser cladded NiAlCrZrMo medium–entropy alloy coating by DFT calculation

Microstructure, corrosion resistance and high temperature oxidation properties of AlCrFeNiCu high-entropy alloy coating by high-speed laser cladding

Stepwise Laser Cladding of TiNbZr and TiTaZr Medium-Entropy Alloys on Pure Ti Substrate

Microstructural characterization and corrosion behaviour of AlCoCrFeNiTix high-entropy alloy coatings fabricated by laser cladding

Effect of annealing on microstructure and mechanical properties of AlCrFe2Ni2 medium entropy alloy fabricated by laser powder bed fusion additive manufacturing

Effect of Heat Treatment on Microstructure and Wear Behavior of Laser Clad FeCoCrMoNi High-Entropy Alloy Coatings

Effect of Laser Parameters on the Microstructure and Properties of CoCrFeNiMn High Entropy Alloy Coatings

Effect of Ti Content on the Microstructure and Corrosion Resistance of CoCrFeNiTix High Entropy Alloys Prepared by Laser Cladding

Preparation of CrCoFeNiMn High-Entropy Alloy Coatings Using Gas Atomization and Laser Cladding: An Investigation of Microstructure, Mechanical Properties, and Wear Resistance

Microstructure and elevated temperature wear behavior of laser-cladded AlCrFeMnNi high-entropy alloy coating

Effect of Laser Energy Density on the Properties of CoCrFeMnNi High-Entropy Alloy Coatings on Steel by Laser Cladding

Microstructure and corrosion behavior of Co-free FeCrNiSi0.4 medium entropy alloy coating fabricated by laser cladding

Microstructure and wear behavior of mechanically alloyed powder AlxMo0.5NbFeTiMn2 high entropy alloy coating formed by laser cladding

Wear-Resistant Fe6AlCoCrNi Medium-Entropy Alloy Coating Made by Laser Cladding

New lightweight high-entropy alloy coatings: Design concept, experimental characterization, and high-temperature oxidation behaviors

Corrosion behavior of Al0.4CoCu0.6NiSi0.2Ti0.25 high-entropy alloy coating via 3D printing laser cladding in a sulphur environment

Study on Microstructure and Properties of AlCoCrFeNi High-Entropy Alloys by Extreme High-Speed Laser Cladding

Investigation of the Microstructure and Properties of CoCrFeNiMo High-Entropy Alloy Coating Prepared through High-Speed Laser Cladding

Laser additively manufacturing of Al0.5CoCrFeNiTi0.5 high-entropy alloys with increased resistances to corrosion 3.5% NaCl and oxidation at 1000 °C

Influence of Microstructure Evolution on the Electrochemical Corrosion Behavior of (CoCrFeNi)94Ti1.5Al4.5 High Entropy Alloy Coatings

Microstructure and corrosion behavior of CeO2/FeCoNiCrMo high-entropy alloy coating prepared by laser cladding