Iodine-Substituted Lithium/Sodium closo -Decaborates: Syntheses, Characterization, and Solid-State Ionic Conductivity
Shouhu Li,Pengtao Qiu,Jiaxin Kang,Yiming Ma,Yichun Zhang,Yigang Yan,Torben R. Jensen,Yanhui Guo,Jie Zhang,Xuenian Chen
DOI: https://doi.org/10.1021/acsami.1c01659
2021-04-06
Abstract:Solid-state electrolytes based on <i>closo</i>-decaborates have caught increasing interest owing to the impressive room-temperature ionic conductivity, remarkable thermal/chemical stability, and excellent deformability. In order to develop new solid-state ion conductors, we investigated the influence of iodine substitution on the thermal, structural, and ionic conduction properties of <i>closo</i>-decaborates. A series of iodinated <i>closo</i>-decaborates, M<sub>2</sub>[B<sub>10</sub>H<sub>10–<i>n</i></sub>I<sub><i>n</i></sub>] (M = Li, Na; <i>n</i> = 1, 2, 10), were synthesized and characterized by thermal analysis, powder X-ray diffraction, and electrochemical impedance spectroscopy; the stability and ionic conductivity of these compounds were studied. It was found that with the increase of iodine substitution on the <i>closo</i>-decaborate anion cage, the thermal decomposition temperature increases. All M<sub>2</sub>[B<sub>10</sub>H<sub>10–<i>n</i></sub>I<sub><i>n</i></sub>] exhibit an amorphous structure. The ionic conductivity of Li<sub>2</sub>[B<sub>10</sub>H<sub>10–<i>n</i></sub>I<sub><i>n</i></sub>] is higher than that of the Li<sub>2</sub>[B<sub>10</sub>H<sub>10</sub>] parent compound. An ionic conductivity of 2.96 × 10<sup>–2</sup> S cm<sup>–1</sup> with an activation energy of 0.23 eV was observed for Li<sub>2</sub>[B<sub>10</sub>I<sub>10</sub>] at 300 °C, implying that iodine substitution can improve the ionic conductivity. However, the ionic conductivity of Na<sub>2</sub>[B<sub>10</sub>H<sub>10–<i>n</i></sub>I<sub><i>n</i></sub>] is lower than that of Na<sub>2</sub>[B<sub>10</sub>H<sub>10</sub>] and increases with the increase of iodine substitution, which could be associated with the increase of the electrostatic potential, mass, and volume of the iodinated anions. Moreover, Li<sub>2</sub>[B<sub>10</sub>I<sub>10</sub>] offers a Li-ion transference number of 0.999, an electrochemical stability window of 3.3 V and good compatibility with the Li anode, demonstrating its potential for application in high-temperature batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c01659?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c01659</a>.NMR, mass, and FTIR spectra of the as-synthesized M<sub>2</sub>[B<sub>10</sub>H<sub>10–<i>n</i></sub>I<sub><i>n</i></sub>] (M = Li, Na; <i>n</i> = 1, 2, 10) compounds; <sup>11</sup>B NMR spectra of M<sub>2</sub>[B<sub>10</sub>H<sub>10–<i>n</i></sub>I<sub><i>n</i></sub>] (M = Li, Na; <i>n</i> = 1, 2, 10) recorded after being heated to a given temperature; FTIR spectra of M<sub>2</sub>[B<sub>10</sub>H<sub>8</sub>-1,10-I<sub>2</sub>] (M = Li, Na) recorded before and after being heated to 300 °C; and the electrochemical performance of Li<sub>2</sub>[B<sub>10</sub>I<sub>10</sub>] (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c01659/suppl_file/am1c01659_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology