Abstract:To explore the influence of the interface properties between fiber/cement matrix on the performance of fiber‐modified cement‐based composite. Polyethylene (PE) and polyvinyl alcohol fiber (PVA) are brought in the cement‐based materials to prepare mortar and Engineered Cementitious Composite (ECC) samples. The mortar's mechanical, and ECC's tensile capacity, four‐point bending and porosity were tested to verify the interface's influence on samples' performance. Furthermore, the water contact angle was used to analyze the wettability of the fiber, and a scanning electron microscope (SEM) was used to observe the fiber/matrix interface on the microscopic scale. Molecular dynamics simulation was performed to calculate the interfacial paraments from an atomic scale. The results shows that fiber increases the toughness of the mortar and improved its flexural strength. Through SEM, it was found that PVA fiber can form tight adsorption with the hydration matrix. While there are many apparent cracks and pores at the PE/matrix interface, the poor bonding destroys the matrix's structure and reduces its compressive strength. By analyzing the performance of ECC samples, it was known that PVA‐ECC's strain rate can reach 5.73%, while PE‐ECC is 4.20%. PE fiber has higher mechanical strength and can bear more loads, it helps PE‐ECC to obtain a greater modulus of rapture. Nuclear magnetic resonance results showed that the porosity of PVA‐ECC is lower than PE‐ECC. The ability of PE‐ECC to resist external interference is weak, and the interface of PE/matrix is easily damaged. Molecule dynamics simulation results indicated the adsorption energy between PVA/CSH is 6.17 times that of PE/CSH. The PVA/C‐S‐H interface tends to form CaO and H‐bonds to strengthen the bonding, the bonding has limited the movement of atoms and making the PVA chains tightly adsorbed on the CSH surface. While the adsorption between PE and CSH is weak, the PE will detach from the CSH surface and form aggregates. Moreover, PVA and water molecules form a stable hydrogen bond network to promote the hydration production grows on the surface of PVA fiber. However, PE fiber is complex enough to adsorb water molecules and hardly encourage the development of pores at the interface. By analyzing the properties of the interface between different fibers and cement matrix can provide insights for strengthening the interface properties of fiber cement matrix, and then improve the properties of fiber cement‐based composites.

Effects of thickener on macro- and meso-mechanical properties of ECC

Mechanical Properties and Carbonation Durability of Engineered Cementitious Composites Reinforced by Polypropylene and Hydrophilic Polyvinyl Alcohol Fibers

Influence of Hydroxypropyl Methylcellulose Dosage on the Mechanical Properties of 3D Printable Mortars with and without Fiber Reinforcement

Effect of Textile Layers and Hydroxypropyl Methylcellulose on Flexural Behavior of TRLC Thin Plates

Effects of Redispersible Polymer Powders on the Structural Build-Up of 3D Printing Cement Paste with and Without Hydroxypropyl Methylcellulose

Rheological Properties and Early-Age Microstructure of Cement Pastes with Limestone Powder, Redispersible Polymer Powder and Cellulose Ether

Optimisation of the Mechanical Properties and Mix Proportion of Multiscale-Fibre-Reinforced Engineered Cementitious Composites

Effects of Hydroxypropyl Methylcellulose on Physicochemical Properties and Microstructure of κ-Carrageenan Film

Effects of additives on the mechanical properties, rheology, and printing properties of Pcc-based 3DPMs

Regulating the mechanical properties and microporous structures of hydroxypropyl methylcellulose based microporous photophobic films by adjusting the l-ethyl-3-methylimidazolium acetate content

Effect of interfacial properties between polyethylene and polyvinyl alcohol fiber/cement matrix on properties of mortar and ECC

Effects of fiber volume fraction, fiber length, water-binder ratio, and nanoclay addition on the 3D printability of strain-hardening cementitious composites (SHCC)

Relationship between microstructure and strain-hardening behaviour of 3D printed engineered cementitious composites

Effects of HPMC on Workability and Mechanical Properties of Concrete Using Iron Tailings as Aggregates

Multiscale Investigation on the Performance of Engineered Cementitious Composites Incorporating PE Fiber and Limstone Calcined Clay Cement (LC3)

Controllable Synthesis and Rheological Characterization of Hydroxypropyl Methyl Cellulose

Water Retention Mechanism of HPMC in Cement Mortar

Synthesis of C-S-H accelerating admixture and its effect on mechanical and hydration properties of engineering cementious composites

Effects of xylan-modified precipitated calcium carbonate filler on the properties of paper

Comparative Study on the Effects of Various Modified Admixtures on the Mechanical Properties of Styrene-Acrylic Emulsion-Based Cement Composite Materials

Effects of interface bonding on the macro-mechanical properties of microcapsule/epoxy resin composites