Abstract:A series of desiccation tests were performed to investigate the effects of both interfacial friction and layer thickness on desiccation cracking behavior of soil. Nine groups of slurry specimens with different interfacial roughness and layer thicknesses were prepared and dried under a constant temperature of 30 °C. During drying, the change in water content was recorded and the dynamic process of soil cracking was monitored with a digital camera at different time intervals. Using digital image processing technique, the propagation characteristics of desiccation cracks on soil sample surfaces were quantitatively described with a series of geometric parameters. The results show that the initiation and propagation of cracks occur at relatively high water content ranging from 10% to 40% during drying. For the same soil layer thickness, the larger the interfacial roughness, the faster the propagation velocity of soil cracks. However, the influence of interfacial friction on soil cracking decreases with increase in soil layer thickness. Besides, there is a negative linear relationship between soil layer thickness and peak propagation velocity of soil cracks. During drying, the critical water content (wf, refers to the water content when the propagation of soil cracks tends to stabilize) decreases with increase in interfacial roughness under the same soil layer thickness. The final morphology of the desiccation crack network on each soil sample is significantly influenced by both the interfacial friction and soil layer thickness. The intensity of soil cracking increases with increase in interfacial roughness or decrease in soil layer thickness. These results also confirm that the effects of interfacial friction and layer thickness on soil desiccation cracking are coupled. Generally, the interface friction effect is more pronounced for thinner soil layers.

Drying and cracking mechanisms in a starch slurry

Morphometric analysis of polygonal cracking patterns in desiccated starch slurries

Numerical study of drying process and columnar fracture process in granules-water mixtures

Cracking to Curling Transition in Drying Colloidal Films

Universal Scaling of Polygonal Desiccation Crack Patterns

Desiccation of a clay film: Cracking versus peeling

An Experimental Investigation of the Scaling of Columnar Joints

Crack formation and self-closing in shrinkable, granular packings

Crack densification in drying colloidal suspensions

Experimental Investigation of the Desiccation Cracking Behavior of Soil Layers During Drying

Insight into the Initiation and Propagation Mechanism of Desiccation Cracking in Clayey Soil from DEM Simulations

Capillary stress and structural relaxation in moist granular materials

Drought‐Induced Soil Desiccation Cracking Behavior with Consideration of Basal Friction and Layer Thickness

Coupling effects of interfacial friction and layer thickness on soil desiccation cracking behavior

Desiccation Cracking Behavior of Soils

Influence of drying conditions on the stress and weight development of capillary suspensions

On maturation of crack patterns

Desiccation and Relaxation Regimes in Fracture of Drying Clay Films

Nucleation and propagation mechanisms of soil desiccation cracks

Morphology characterization of unsaturated soils under drying-wetting cycles: crack opening and closure

Fracture Morphology of Desiccation Cracks in Clayey Soil