Abstract:1 Laboratory tests were conducted to investigate the effect of wetting-drying (W-D) 2 cycles on the initiation and evolution of cracks in clay layer. Four identical slurry 3 specimens were prepared and subjected to five subsequent W-D cycles. The water 4 evaporation, surface cracks evolution and structure evolution during the W-D cycles 5 were monitored. The effect of W-D cycles on the geometric characteristics of crack 6 patterns was analyzed by image processing. The results show that the desiccation and 7 cracking behaviour was significantly affected by the applied W-D cycles: the 8 measured cracking water content θ c , surface crack ratio R sc and final thickness h f of 9 the specimen increased significantly in the first three W-D cycles and then tended to 10 reach equilibrium; the formed crack patterns after the second W-D cycle were more 11 irregular than that after the first W-D cycle; the increase of surface cracks was 12 accompanied by the decrease of pore volume shrinkage during drying. In addition, it 13 was found that the applied W-D cycles resulted in significant rearrangement of 14 specimen structure: the initially homogeneous and non-aggregated structure was 15 converted to a clear aggregated-structure with obvious inter-aggregate pores after the 16 second W-D cycle; the specimen volume generally increased with increasing cycles 17 due to the aggregation and increased porosity. The image analysis results show that 18 the geometric characteristics of crack pattern were significantly influenced by the 19 W-D cycles, but this influence was reduced after the third cycle. This is consistent 20 with the observations over the experiment, and indicates that the image processing can 21 be used for quantitatively analyzing the W-D cycle dependence of clay desiccation 22 cracking behaviour.

Desiccation and Relaxation Regimes in Fracture of Drying Clay Films

Desiccation of a clay film: Cracking versus peeling

Manipulating crack formation in air-dried clay suspensions with tunable elasticity

Cracking to Curling Transition in Drying Colloidal Films

Universal Scaling of Polygonal Desiccation Crack Patterns

Fracture Morphology of Desiccation Cracks in Clayey Soil

Desiccation Cracking Behavior of Soils

On maturation of crack patterns

Crack densification in drying colloidal suspensions

Drying and cracking mechanisms in a starch slurry

Experimental characterization of shrinkage and desiccation cracking in thin clay layer

Spiral Cracks in Drying Precipitates

Deformation Mechanisms of Polymer Thin Films by Simultaneous Kinetic Measurement of Microscopic Infrared Dichroism and Macroscopic Stress. Part Iii: Influence of Morphology on Molecular Orientation of Isotactic Polypropylene Films Subjected to Uniaxial Stretching

Three-dimensional Characterization of Desiccation Cracking Behavior of Compacted Clayey Soil Using X-ray Computed Tomography

Desiccation and Cracking Behaviour of Clay Layer from Slurry State under Wetting–drying Cycles

Factors Affecting the Surface Cracking in Clay Due to Drying Shrinkage

Experimental Investigation of the Desiccation Cracking Behavior of Soil Layers During Drying

Nucleation and propagation mechanisms of soil desiccation cracks

Evolution of polygonal crack patterns in mud when subjected to repeated wetting-drying cycles

Cracking in polymer glasses and evolution at zero stress: Highlighting discrete long time scale relaxations

A study of the dynamic experimental of clay desiccation cracking process