Experimental research on uniaxial tensile mechanical properties of Kapton foils
YAN Liu,YANZHEN Liu
DOI: https://doi.org/10.1007/s10965-022-03123-1
IF: 3.061
2022-06-16
Journal of Polymer Research
Abstract:To reveal the strength and stiffness characteristics of Kapton foils in detail, axial and off-axial tensile tests were conducted systematically. First, Kapton foils with a thickness of 25 μm were used, and the strip specimens were manufactured according to the machine direction (MD) and the transverse direction (TD) of the foils. The stress–strain curves of the foils were obtained under five constant strain rates (10, 25, 50, 100, and 200 mm/min). Based on the stress–strain curves, the tensile strength, elongation at break, equivalent yielding stress, yielding strain and elastic modulus were analyzed and calculated. Based on the results and analysis, some useful findings were derived. The stress–strain curves showed obvious nonlinearity; and there were at most four main stages of approximate elasticity, elasticity-plasticity, plastic flow and strain hardening from the beginning of tension to fracture. The uniaxial tensile mechanical properties of the Kapton foils along the MD and TD are almost identical during the approximate elasticity stage. After that stage, the material showed different mechanical properties in the two directions. By analyzing the mechanical parameters above, quadratic or linear fitting formulas with the tensile rate as the variable were given, which can be used to predict the mechanical parameters of Kapton foils under different strain rates and provide basic data for inflatable deployable structures in the future. Second, for the same samples as above, the tensile tests of seven off-axis angles from 0° to 90° with a step size of 15° were conducted. Based on the obtained stress–strain curves, strength and elongation at break under different angles, the relationships between the elastic modulus and strain were deduced. The results show that Kapton is a typical type of nonlinear and anisotropic material. Additionally, there is an "N"-shaped relationship between the tensile strength and off-axis angles, which is different from the "U"-shaped relationship embodied in the Tsai-Hill strength criterion. The elastic modulus of Kapton foils varies as the off-axis angle changes. The elastic theory of orthotropic plates provides a good prediction of the equivalent elastic modulus of Kapton foils. The results can provide some basic references for the strength prediction, deformation calculation, and design and analysis of inflatable deployable structures.
polymer science