Light-Induced Ammonia Generation over Defective Carbon Nitride Modified with Pyrite
Judith Zander,Roland Marschall
DOI: https://doi.org/10.1149/ma2023-02472321mtgabs
2023-12-22
ECS Meeting Abstracts
Abstract:The challenge to mitigate climate change and to limit global warming to well below 2 °C according to the Paris Agreement, requires a reduction of greenhouse gas emissions not only in transportation, but also in industry.[1] The Haber-Bosch process for the production of ammonia, NH 3 , is one of the most important industrial processes, but significantly contributes to the world’s annual CO 2 emissions.[2] Photocatalytic reduction of dinitrogen (NRR) offers a sustainable alternative for the synthesis of ammonia. Some of the highest activities so far were achieved with carbon nitride (C 3 N 4 ) photocatalysts, especially after the introduction of nitrogen vacancies.[3] Carbon nitrides are earth abundant, non-toxic, low-cost polymeric materials, with a suitable band gap for visible light absorption. To overcome the inherently fast charge carrier recombination that diminishes the efficiency, heterojunctions with a second photocatalyst are widely investigated.[4] Another common approach in the design of photocatalyst for the NRR is nature-inspired. Herein, mainly sulphur, iron and molybdenum containing materials are investigated, inspired by the composition of the active centre in nitrogenase enzymes.[5] In this contribution we present composite materials of FeS 2 and vacancy-rich V N -C 3 N 4 , thereby combining both strategies of heterojunction formation and bio-inspiration, as well as that of defect engineering in C 3 N 4 , to increase the number of active sites.[6] The composites yield significantly higher amounts of ammonia after light irradiation for 7 h, compared to both FeS 2 and V N -C 3 N 4 alone. Hydrogen is produced as the only by-product. A combination of control experiments and material characterisation before and after light irradiation revealed that iron in FeS 2 coordinates to V N -C 3 N 4 at the defect site. Cyano-groups at these sites are activated via π-back-donation and subsequently converted into ammonia. Thus we could prove that – at least initially – ammonia is generated not from the N 2 gas, but from the C 3 N 4 -framework itself. References: [1] UNFCCC, Adoption of the Paris Agreement, 21 st Conference of the Parties , Paris, 2015 . [2] J. G. Chen, R. M. Crooks, L. C. Seefeldt, K. L. Bren, R. M. Bullock, M. Y Darensbourg, P. L. Holland, B. Hoffman, M. J. Janik, A. K. Jones, M. G. Kanatzidis, P. King, K. M. Lancaster, S. V. Lymar, P. Pfromm, W. F. Schneider, R. R. Schrock, Science 2018 , 360 , 6391. [3] a) W. Wang, H. Zhang, S. Zhang, Y. Liu, G. Wang, C. Sun, H. Zhao, Angew. Chem. Int. Ed. 2019 , 58 , 16644, b) X. Li, X. Sun, L. Zhang, S. Sun, W. Wang, J. Mater. Chem. A 2018 , 6 , 3005. [4] J. Fu, J. Yu, C. Jiang, B. Cheng, Adv. Energy Mater. 2018 , 8 , 1701503. [5] K. Tanifuji, Y. Ohki, Chem. Rev. 2020 , 120 , 5194. [6] J. Zander, J. Timm, M. Weiss, R. Marschall, Adv. Energy Mater . 2022 , 12 , 2202403. Figure 1