Zn(1-x)Cu(x)O (0.02 ≤ x ≤ 0.1) Nanomaterials Prepared by Ball Milling, Citrate Sol Gel, and Molten Salt Flux Methods.

K. Melba,S. Balamurugan

DOI: https://doi.org/10.1166/JNN.2015.9770

2015-06-01

Journal of Nanoscience and Nanotechnology

Abstract:The Cu doped ZnO, (Zn(1-x)Cu(x))O (x = 0.02, 0.04, 0.06, 0.08, and 0.1) nanomaterials were prepared by ball milling technique (BMT), citrate sol gel (CSG), and molten salt flux (MSF) methods. The various as-prepared (Zn(1-x)Cu(x))O materials were analyzed by powder X-ray diffraction (pXRD), FT-IR, and SEM-EDX measurements in order to check the phase formation, purity, surface morphology and elements present in the annealed materials. Due to the preparation methods as well as doping of 'x' slight variations in cell parameters are seen. The average crystalline size of CSG method shows smaller size (25-35 nm) than BMT and MSF approaches. The materials obtained by MSF technique reveal the average crystalline size in the range of 32-72 nm whereas the BMT materials exhibit 36-50 nm for the composition, 0.02 ≤ x ≤ 0.1. The presence of functional groups and the chemical bonding in (Zn(1-x)Cu(x))O system is confirmed through FT-IR measurements. It is evident from the FT-IR data that bands seen at 400-500 cm(-1) are characteristics of M-O (M = metal ion) bonding in the studied materials. The micro images observed by SEM exhibiting polycrystalline character as compared with the crystallite size obtained from XRD. Among the three approaches employed in the present investigations, in terms of average particle size the CSG method may be concluded as an efficient method for the preparation of Zn(1-x)Cu(x)O nanomaterials.

Medicine,Materials Science,Chemistry