Fatigue and Fretting Behaviors of Self-piercing Riveting in Carbon-Fiber-Reinforced Polymer Laminates and Titanium Sheets with Pre-drilling Operation

Xianlian Zhang,Qing Zhang,Baoying Xing,Xiaocong He,Jiawei Lu

DOI: https://doi.org/10.1007/s11665-024-10494-7

IF: 2.3

2024-12-07

Journal of Materials Engineering and Performance

Abstract:With the application of composite laminates in many industries, the drilling of laminates has been a usual machining operation for assembling by bolted or riveted joints. In this work, the effects of drilling operation on the forming structure, fatigue performance, failure and fretting behaviors of SPR joints in dissimilar composites and titanium sheets were investigated systematically. As a result, the forming feature of the joints was changed and the fatigue limit was enhanced effectively by the drilling operation. The delamination and matrix damage occurred in the CFRP laminate under fatigue loading, and the pre-holed joints were damage more seriously. The fretting behavior existed in the contact interface, which played a crucial role on the fatigue failure modes of rivet pull-out, rivet fracture and sheet fracture. A large amount of wear debris was generated between the fracture surfaces, which contributed to initiate secondary cracks and promote crack propagation, ultimately accelerating fatigue failure. Due to drilling operation, the contact angle between the loading direction and contact region was decreased compared with the regular joints and the wear behaviors were affected apparently, so that the failure mode changed from sheet fracture in regular joints to rivet fracture in pre-holed joints at relative lower loads.

materials science, multidisciplinary