Takuya Ohzono,Mohand O. Saed,Youfeng Yue,Yasuo Norikane,Eugene M. Terentjev
Abstract:Smart surfaces that reversibly change the interfacial friction coefficients in response to external stimuli enable a wide range of applications, such as grips, seals, brake pads, packaging films, and fabrics. Here a new concept of such a smart frictional system is reported: a composite film of a plain-weave polyester textile sheet, and a thermo-responsive nematic liquid crystalline elastomer (LCE). The composite is deployed with retractable micro-undulations of the elastomer inside each weave mesh, enabling dramatic changes of the contact interface with the opposing surface on LCE actuation, which is induced e.g. by a change in temperature (T). At ambient T, the protruding viscoelastic parts of LCE in the nematic phase make contact with the opposing flat surface, resulting in a very high friction. At an elevated T (50C, isotropic phase), the undulations of LCE surface are retracted within the thickness of the textile, and the contacts are limited to small regions around overlapping textile fibers, lowering the friction dramatically. This effect is fully reversible on heating/cooling cycles. The surface undulations are spontaneous, i.e. fabricated without any lithographic or alignment techniques. The present composite opens a new way to practical uses of sheets/films with switchable friction enabled by stimuli-responsive LCEs.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is how to design an intelligent surface material that can reversibly change the coefficient of friction according to external stimuli (such as temperature changes). Specifically, the authors proposed a new composite material system, that is, a composite of liquid - crystal elastomer (LCE) and textiles. This composite material can significantly adjust the friction force by changing the microscopic morphology of the contact interface when the temperature changes.
### Background and Objectives of the Paper
1. **Background**:
- Friction is very important in many practical applications, such as gripping, sealing, brake pads, packaging films and fabrics.
- Intelligent contact surfaces that can switch friction characteristics on demand have broad application prospects.
- Traditional friction adjustment methods usually rely on changes in surface topology, but these methods have certain limitations, such as the need to apply macroscopic strain or specific alignment layers.
2. **Objectives**:
- Design a new type of intelligent friction system that can achieve a large - scale change in friction force by changing the contact area and the properties of the contact materials when the temperature changes.
- This system should be able to achieve reversible friction adjustment and remain stable during heating and cooling cycles.
### Core Concepts of the Paper
1. **Material Selection**:
- Use thermally responsive nematic liquid - crystal elastomer (LCE) to composite with plain - weave polyester textiles.
- LCE will undergo a phase change at different temperatures, thereby changing its surface morphology.
2. **Working Mechanism**:
- At room temperature, LCE is in the nematic phase, and its surface forms convex microripples, having a large contact area with the opposite flat surface, resulting in high friction.
- When the temperature rises to about 50 °C, LCE transforms into the isotropic phase, and the microripples on the surface retract into the textile, the contact area decreases, and the friction force is significantly reduced.
- This change is completely reversible and can be repeated in multiple heating and cooling cycles.
### Experimental Results
1. **Surface Morphology Changes**:
- Through microscopic observation, the surface morphology changes of LCE at different temperatures were confirmed.
- At room temperature, the LCE surface is convex, forming microripples; at high temperature, the LCE surface is flat and the ripples disappear.
2. **Friction Force Testing**:
- The static friction coefficient (\(\mu_S\)) and the dynamic friction coefficient (\(\mu_K\)) were measured at different temperatures.
- The results show that at room temperature, the friction coefficients are relatively high (\(\mu_S> 1\), \(\mu_K> 0.6\)), while at high temperature, the friction coefficients are significantly reduced (\(\mu_S < 0.4\), \(\mu_K < 0.2\)).
- The maximum change in the friction coefficient can reach six times.
### Conclusion
This research successfully designed and prepared a composite material based on LCE and textiles, which can achieve a large - scale reversible adjustment of the friction force when the temperature changes. This material has broad application prospects, especially in the fields of robotic hands, touch - screen devices and intelligent textiles. Through a simple non - photolithographic manufacturing method, this composite material shows excellent performance and reliability.