Thermal weakening of cracks and brittle-ductile transition: a phase model

Tom Vincent-Dospital,Renaud Toussaint,Alain Cochard,Knut Jørgen Måløy,Eirik G. Flekkøy

DOI: https://doi.org/10.1103/PhysRevMaterials.4.023604

2020-02-25

Abstract:We present a model for the thermally activated propagation of cracks in elastic matrices. The propagation is considered as a subcritical phenomenon, the kinetics of which being described by an Arrhenius law. In this law, we take the thermal evolution of the crack front into account, assuming that a portion of the released mechanical energy is transformed into heat in a plastic process zone. We show that such a model leads to a two-phase crack propagation: a first phase at low velocity in which the temperature elevation is of little effect and the propagation is mainly governed by the mechanical load and by the toughness of the medium, and a second phase in which the crack is thermally weakened and propagates at greater velocity. Such a dual behavior can potentially explain the usual stick-slip in brittle fracturing, and we illustrate how with numerical simulations of mode I cracks propagating in thin disordered media. In addition, we predict the existence of a limiting ambient temperature above which the weakened phase ceases to exist and we propose this critical phenomenon as a novel explanation for the brittle-ductile transition of solids.

Materials Science,Geophysics

What problem does this paper attempt to address?

The problem that this paper attempts to solve is about the dynamic behavior of crack propagation in materials during the stress - bearing process, especially the influence of temperature on the crack propagation process. Specifically, the authors proposed a crack propagation model based on thermal activation, aiming to explain the brittle - plastic transition phenomenon of materials under different temperature conditions. This model takes into account the local temperature rise at the crack tip due to the release of mechanical energy and how this temperature rise in turn affects the crack propagation speed. Through this model, the authors hope to be able to explain some common fracture mechanics phenomena, such as the stick - slip phenomenon in brittle materials, and propose a new mechanism to explain the brittle - plastic transition of solid materials.

The core of the model is an Arrhenius law, which is used to describe the relationship between the crack propagation speed and temperature. The formula involved is:

\[ V = V_0 e^{\frac{\alpha^2 (G - G_c)}{k_B (T_0 + \Delta T(V, G))}} \]

Here, \( V \) is the crack propagation speed, \( V_0 \) is the maximum crack speed, \( \alpha \) is the characteristic size of the crack process, \( G \) is the energy release rate, \( G_c \) is the fracture energy of the material, \( k_B \) is the Boltzmann constant, \( T_0 \) is the ambient temperature, and \( \Delta T(V, G) \) is the temperature rise at the crack tip.

Through this model, the authors predicted the two - phase behavior of the crack propagation speed \( V \) under different mechanical loads \( G \) and ambient temperatures \( T_0 \): the low - speed phase and the high - speed phase. In the low - speed phase, the temperature rise has a relatively small impact on crack propagation; in the high - speed phase, the temperature at the crack tip rises significantly, resulting in an accelerated crack propagation speed. In addition, the model also predicts that there is a critical ambient temperature \( T_0^* \), above which the high - temperature phase no longer exists and the fracture behavior of the material changes from brittle to plastic.

These theoretical results not only help to understand the basic mechanisms of material fracture, but may also provide a new perspective for the study of geological disasters such as earthquakes.