Abstract:The anisotropic ductile fracture behavior of a stainless steel is investigated using a combination of experiments and analysis. The material is SS-304L, an austenitic, low-carbon stainless steel, received in the form of tubes of 2.38 mm dia. and 0.15 mm thickness. The tubes are inflated under volume control in a custom apparatus. At the same time, the axial force on the tubes is kept proportional to the pressure induced by the inflation. This leads to quasi-proportional stress paths in the meridional-hoop engineering stress space. A total of 15 discrete paths are successfully tested. Stereo-type Digital Image Correlation is used to measure the strains. In every case, the tubes develop a series of instabilities before bursting. The failure is oriented along the meridional or the hoop direction of the tube, depending on which stress is greater. A mild plastic anisotropy is detected in these experiments. Hence these results are then used for calibrating the anisotropic yield criterion Yld2004-3D. This is introduced in a finite element model of the experiments, which includes a thickness imperfection designed to capture the two failure orientations observed in the experiments. The numerical model using the Yld2004-3D criterion reproduces the experiments well, e.g., it captures the experimental stress-strain and induced strain paths better than von Mises. It is then used to probe the conditions at the onset of fracture (hybrid method). It is found that most paths lead to essentially proportional loading during deformation. A significant anisotropy in the fracture behavior is detected, with the meridional-stress-dominated paths being able to develop much higher strains than the hoop-dominated ones. These results are then captured by the DF2016 ductile fracture criterion, modified to use the anisotropic yield criterion Yld91. The proposed criterion is flexible enough to represent the fracture anisotropy very well, without being unnecessarily complex. The fracture forming limit curve (i.e., the fracture envelope in strain space) predicted by the DF2016/Yld91 model is also found to be very close to the experiments. The results and findings of this work help establish a framework to reliably design components and processes when significant fracture anisotropy is expected.

A Methodology to Assess Directional and Spatial Variations of Tensile and Fracture Properties in Fabricated Nuclear Components

Use of instrumented indentation testing to study local mechanical properties of 304L SS welded joints subjected to low-cycle fatigue loadings

Study of Ligament Length Effect on Mode Mix of a Modified In-Plane Shear Test Specimen

In-situ observations on local fracture behavior in a dissimilar metal weld joint of nuclear power plant

A correlation-based approach for evaluating mechanical properties of nuclear fuel cladding tubes

A New Approach to Evaluate Fracture Toughness of Structural Materials

Analysis of Interlaminar Fracture Toughness and the Mechanical Properties of Composite Cylinders

Anisotropic Ductile Fracture Of A Stainless Steel Under Biaxial Loading: Experiments And Predictions

Fracture Studies on Cruciform Bend Specimens of Pressure Vessel Steel subjected to Thermo-mechanical Loading

Prediction of static failure in metal inert gas welded nuclear grade pipe 347 SS: Experimentation and finite-element analysis approach

An Experimental Investigation of In-Plane Constraint Effect on Local Fracture Resistance of A Dissimilar Metal Welded Joint

Experimental and Numerical Fracture Characterization of DP1180 Steel in Combined Simple Shear and Uniaxial Tension

Numerical Investigation of Ductile Crack Growth Behavior in a Dissimilar Metal Welded Joint

Incorporation of Obstacle Hardening into Local Approach to Cleavage Fracture to Predict Temperature Effects in the Ductile to Brittle Transition Regime

Experimental study on fatigue crack growth behavior and fracture toughness of SA508-III steel for nuclear reactor pressure vessel

Combined evaluation of Young modulus and fracture toughness in small specimens of fine grained nuclear graphite using 3D image analysis

Low constraint fracture toughness testing for master curve reference temperature determination using 10 mm-thick SE(B) and SE(T) specimens

Experimental Characterisation and Numerical Modelling of Residual Stresses in a Nuclear Safe-End Dissimilar Metal Weld Joint

Experimental evaluation of orientation and temperature dependent material stress-strain curves of Zr2.5%Nb Indian pressure tube material and development of a suitable anisotropic material model

Local fracture behavior in an Alloy 52M dissimilar metal welded joint in nuclear power plants

Alternative Approach to Model Ductile Fracture by Incorporating Anisotropic Yield Function