Application of Three-Dimension Printing Nano-Carbonated-Hydroxylapatite to the Repair of Defects in Rabbit Bone
Shujie Wang,Chunyan Shao,Xingkai Zhao,Yizhe Guo,Houhui Song,Lida Shen,Zhenlei Zhou,Zhen Li
DOI: https://doi.org/10.2147/ijn.s439775
IF: 7.033
2024-02-21
International Journal of Nanomedicine
Abstract:Shujie Wang, 1, 2 Chunyan Shao, 2 Xingkai Zhao, 1 Yizhe Guo, 1 Houhui Song, 2 Lida Shen, 3 Zhenlei Zhou, 1 Zhen Li 4, 5 1 College of Veterinary Medicine, Nanjing Agricultural University, Nanjing, Jiangsu, 210095, People's Republic of China; 2 College of Animal Science and Technology & College of Veterinary Medicine, Zhejiang Agriculture and Forestry University, Hangzhou, Zhejiang, 311300, People's Republic of China; 3 College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing, Jiangsu, 210016, People's Republic of China; 4 College of Resources and Environmental Sciences, Nanjing Agricultural University, Nanjing, Jiangsu, 210095, People's Republic of China; 5 State Key Laboratory of Palaeobiology and Stratigraphy, Nanjing Institute of Geology and Palaeontology and Center for Excellence in Life and Paleoenvironment, Chinese Academy of Sciences, Nanjing, Jiangsu, 210008, People's Republic of China Correspondence: Zhenlei Zhou, College of Veterinary Medicine, Nanjing Agricultural University, Nanjing, Jiangsu, 210095, People's Republic of China, Tel +86 (25) 84395505, Email Zhen Li, College of Resources and Environmental Sciences, Nanjing Agricultural University, Nanjing, Jiangsu, 210095, People's Republic of China, Tel/Fax +86 (25) 84399827, Email Introduction: Hydroxylapatite (HAp) is a biodegradable bone graft material with high biocompatibility. However, the clinical application of HAp has been limited due to the poor absorption rate in vivo. Methods: In this study, carbonated hydroxylapatite (CHAp) with a chemical composition similar to natural bone was synthesized. HAp and CHAp scaffolds were fabricated by 3D printing. Each material was designed by two types of scaffold model with a maximum width of 8 mm and a thickness of 2 mm, ie, structure I (round shape) and structure II (grid shape). Then, the HAp scaffolds were loaded with lutein. These scaffolds were implanted into the 8 mm bone defect on the top of the rabbit skull within 3 hours in the morning. The curative effects of the scaffolds were assessed two months after implantation. Results: The 3D printed scaffolds did not cause severe inflammation or rejection after implantation. It showed that the porous structures allow bone cells to enter into the scaffolds. Furthermore, CHAp scaffolds were more biocompatible than HAp scaffolds, and showed a higher level of degradation and new bone formation after implantation. Structure II scaffolds with a smaller mineral content degraded faster than structure I, while structure I had better osteoconductive properties than structure II. Besides, the addition of lutein significantly enhanced the rate of new bone formation. Discussion: The uniqueness of this study lies in the synthesis of 3D printed CHAp scaffolds and the implantation of CHAp in rabbit bone defects. The incorporation of suitable carbonate and lutein into HAp can enhance the osteoinductivity of the graft, and CHAp has a faster degradation rate in vivo, all of which provide a new reference for the research and application of apatite-based composites. Keywords: bone, 3D printing, hydroxylapatite, lutein, repair The bone defect caused by severe trauma, infection, tumor resection, etc. requires bone grafting for better recovery. 1,2 It is estimated that over 2.2 million orthopedic procedures involving bone grafting are performed worldwide annually. 3 Both autologous and allogeneic bone grafts offer significant advantages in osteo-regeneration. 4–7 However, secondary bone damage, complications, or immune rejection might limit the clinical use of graft materials. 8–10 The emergence of synthetic bone substitutes offers more options for bone grafting, and ceramic-based bone substitutes account for about 60% of the synthetic graft market. 11 Hydroxylapatite (HAp) has a similar chemical composition analogous to natural bone minerals. 12,13 It has excellent biocompatibility, osteoconductivity, and osteoinductivity in bone regeneration. 14–16 However, the relatively high Ca/P ratio and crystallinity of HAp delay the resorption rate in vivo. 17 The bone mineral is a variety of HAp, ie, carbonated-hydroxylapatite (CHAp), with the incorporation of 4–8 wt.% carbonate. 18 CHAp is able to promote initial bone regeneration during the repair of bone defects. 14,19 In addition, CHAp shows high dissolution capability in body physiological environment (pH 7.4). 20 A previous study has reported faster degradation of CHAp in a rat shin defect compared to other calcium phosphate c -Abstract Truncated-
pharmacology & pharmacy,nanoscience & nanotechnology