Abstract:We have studied the structural behavior of bismuth phosphate under compression. We performed x-ray powder diffraction measurements up to 31.5 GPa and ab initio calculations. Experiments were carried out on different polymorphs; trigonal (phase I) and monoclinic (phases II and III). Phases I and III, at low pressure (0.2-0.8 GPa), transform into phase II, which has a monazite-type structure. At room temperature, this polymorph is stable up to 31.5 GPa. Calculations support these findings and predict the occurrence of an additional transition from the monoclinic monazite-type to a tetragonal scheelite-type structure (phase IV). This transition was experimentally found after the simultaneous application of pressure (28 GPa) and temperature (1500 K), suggesting that at room temperature the transition might by hindered by kinetic barriers. Calculations also predict an additional phase transition at 52 GPa, which exceeds the maximum pressure achieved in the experiments. This transition is from phase IV to an orthorhombic barite-type structure (phase V). We also studied the axial and bulk compressibility of BiPO4. Room-temperature pressure-volume equations of state are reported. BiPO4 was found to be more compressible than isomorphic rare-earth phosphates. The discovered phase IV was determined to be the less compressible polymorph of BiPO4. On the other hand, the theoretically predicted phase V has a bulk modulus comparable with that of monazite-type BiPO4. Finally, the isothermal compressibility tensor for the monazite-type structure is reported at 2.4 GPa showing that the direction of maximum compressibility is in the (010) plane at approximately 15 (21) degrees to the a axis for the case of our experimental (theoretical) study.

Synthesis, crystal structure, and characterization of two bismuth phosphates Rb2CaBi2P4O15 and Rb3SrBiP4O14

Synthesis, Crystal Structure and Characterizations of a New Diphosphate Rb2CaP2O7

Phosphates with Two Types of Isolated P-O Groups: Noncentrosymmetric Na 6 Sr 2 Bi 3 (PO 4 )(P 2 O 7 ) 4 and Centrosymmetric Cs 2 CaBi 2 (PO 4 ) 2 (P 2 O 7 )

Influence of Cation on the Anion Frameworks and Properties of Four Lead Phosphates, A<sub>2</sub>PbBi<sub>2</sub>(PO<sub>4</sub>)<sub>2</sub>(P<sub>2</sub>O <sub>7</sub>) (A = Rb, Cs) and A<sub>2</sub>PbP<sub>2</sub>O<sub>7 </sub>(A = K, Rb)

Synthesis, Crystal Structure and Optical Properties of a New Lead Bismuth Borate

High-pressure Synthesis and Structural Characterization of Three New Polyphosphides, Α-Srp3, BaP8, and LaP5

Two Noncentrosymmetric Bismuth Phosphates: Rational Design Synthesis and Optical Properties.

Exploration of the structure, electronic and optical properties of AB 2 (PO 3 ) 5 polyphosphates: a first-principle approach

Synthesis, characterization, and theoretical analysis of three new nonlinear optical materials K7MRE2B15O30 (M= Ca and Ba, RE= La and Bi)

Three Diphosphates, Α-Li2na2p2o7, Li8Pb3Ba(P2O7)4 and Li7Rb(P2O7)2: Influences of Co-Substitution on the Crystal Structure.

Exploring the high-pressure behavior of the three known polymorphs of BiPO4: Discovery of a new polymorph

Bismuth Borates: Two New Polymorphs of Bib3o6

Cyclophosphate MBi(P4O12) (M = Cs, Rb): Structure Change Giving Rise to Property Enhancement

Synthesis and characterization of MxNb4P2O17

Syntheses and Crystal Structures of Two New Bismuth Hydroxyl Borates Containing [bi2o2]2+ Layers: Bi2O2[B3O5(OH)] and Bi2O2[BO2(OH)].

Synthesis, Crystal Structure, and Photoelectric Properties of a New Layered Bismuth Oxysulfide

Synthesis and Crystal Structural Characterization of a New Lead Oxide Chromate Phosphate: Pb5O(CrO4)(PO4)2

(H 3 O)Ca 2 Zn 3.5 (PO 4 ) 4 and Ba 2 Cd 3 (PO 4 ) 2 (HPO 4 ) 2 : Syntheses, Crystal Structures and Characterizations of Two Mixed Metal Phosphates

Synthesis and Characterization of Novel Barium Iron Phosphates: Insight into New Structure Types Tailored by Hydrogen Atoms

Synthesis and Crystal Structure of Sr3Bi2O6 and Structural Change in the Strontium-Bismuth-oxide System

Synthesis and crystal growth of novel layered bismuthides ATM2Bi2, (A = K, Rb; TM = Zn, Cd) with significant electron-deficient structure