Abstract:Acicular ferrite (AF) has been regarded as the optimal microstructure in steel welds and heat affect zones (HAZs), because of its superior combination of strength and toughness. Although various aspects of AF have been investigated, the crystallographic characteristics of AF, including orientation relationship, variant selection and variant pairing, are still not fully studied. In this research, a Ti-deoxidized high strength low alloy steel was prepared and subjected to HAZ thermal cycle simulation tests to attain AF microstructure. Optical micrographs were obtained and EBSD mappings of AF microstructures were conducted. Through crystallographic analysis, the orientation relationship between AF and austenite was found close to that of bainite transformed at a high temperature (580 °C). In the AF microstructure, all 24 variants are formed and variant selection is nearly random. Compared with bainite, the variant pairing of AF is more random despite the slight favour of certain variant pairs. Most of the adjacent AF laths are from different close-packed plane (CP) groups, leading to the classic interlocking morphology. Meanwhile, a large number of neighbouring AF laths belong to different Bain groups, resulting in a high density of high angle grain boundaries (HAGBs). Intragranular nucleation of primary AF laths on inclusions contributes both to the high HAGB density and to the interlocking morphology of AF, while the sympathetic nucleation of secondary AF laths only contributes to the latter. These results suggest that to increase the HAGB density in AF, promoting the intragranular nucleation on inclusions is more important than enhancing the sympathetic nucleation.

Acicular ferrite nucleation mechanism in laser-MAG hybrid welds of X100 pipeline steel

Generation of Acicular Ferrite in the Laser‐Welded Weld of X100 Pipeline Steel Induced by CO2 Shielding Gas

Effect of Ti content on the inclusions, microstructure and fracture mechanism of X100 pipeline steel laser-MAG hybrid welds

Nucleation of Intragranular Acicular Ferrite in the Heat Affected Zone of Ti-Bearing Hsla Steel

The Mechanism of Intragranular Ferrite Nucleation on Inclusion in Steel

The formation mechanisms of interlocked microstructures in low-carbon high-strength steel weld metals

Microstructure and Mechanical Properties of Fiber Laser-Metal Active Gas Hybrid Weld of X80 Pipeline Steel

Molten Pool Behavior and Solidification Characterization in Steady Magnetic Field Assisted Laser-Mig Hybrid Welding of Aluminum Alloy

Corrosion resistance and mechanism of X100 pipeline steel laser-metal active gas hybrid welds with Cr containing welding wire in NS 4 solution

The Defects and Microstructure in the Fusion Zone of Multipass Laser Welded Joints with Inconel 52m Filler Wire for Nuclear Power Plants

Nucleating Acicular Ferrite with Galaxite (Al2O3MnO) and Manganese Oxide (MnO2) in FeMnAlC steels

Inclusion Evolution Behavior of Ti-Mg Oxide Metallurgy Steel and Its Effect on a High Heat Input Welding HAZ

Characteristics of microstructures in laser spot welds of a sintered NdFeB permanent magnet under different welding modes

Microstructural Inhomogeneity in the Fusion Zone of Laser Welds

Influence of Inclusions on the Nucleation of Acicular Ferrites in a Ti–Zr‐Bearing Steel

Interface characteristics and reaction mechanism of steel/Al welds produced by magnetic field assisted laser welding-brazing

The research on weld pool morphology and passive film characteristic of high-nitrogen stainless laser-arc hybrid weld joint

In-Situ Observation On The Influences Of Ti On Phase Transformation Of Weld Metal Processed By High-Heat Input Welding

Three-Dimensional Morphology and Growth Behavior of Acicular Ferrite in Low Carbon Steel Weld

Inclusions Evolution of Ca‐Treated Steel During High‐Heat Input Welding

Crystallographic characteristics of acicular ferrite nucleated on inclusions in a HSLA steel