Abstract:Manganese oxides with varied Mn valance states but identical morphologies were synthesized via a facile thermal treatment of γ-MnOOH. Also, their catalytic performance on ozone decomposition was investigated following the order of Mn3O4 < Mn2O3 < MnO2 < MnO2-H-200. In combination with X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer–Emmett–Teller (BET), transmission electron microscopy (TEM), H2-temperature-programmed reduction (TPR), O2-temperature-programmed desorption (TPD), and X-ray photoelectron spectroscopy (XPS) characterization, it was deduced that the superior O3 decomposition capacity for MnO2-H-200 was strongly associated with abundant oxygen vacancies on its surface. Among Mn3O4, Mn2O3, and MnO2, the difference in O3 decomposition efficiency was dependent on the divergent nature of oxygen vacancy. Density functional theory (DFT) calculation revealed that Mn3O4 and MnO2 possessed lower formation energy of oxygen vacancy, while MnO2 had the minimum desorption energy of peroxide species (O2*). It was deduced that the promotion of the O3 decomposition capability was attributed to the easier O2* desorption. Insights into the deactivation mechanism for MnO2-H-200 further validated the assumptions. As the reaction proceeded, adsorbed oxygen species accumulated on the catalyst surface, and a portion of them were transformed to lattice oxygen. The consumption of oxygen vacancy led to the deactivation of the catalyst.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.langmuir.0c02841?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.langmuir.0c02841</a>.Catalyst preparation; catalyst characterization; XRD patterns of the as-prepared γ-MnOOH; N2 adsorption and desorption isotherms of different MnOx catalysts; top plane view and the oxygen vacancy sites of the preferentially exposed crystal plane for various MnOx during DFT calculation; FT-IR spectra of MnO2-H-200 and partially deactivate MnO2-H-200 catalysts; ozone conversion over MnO2-H-200 and the regenerated MnO2-H-200; the pore size distribution of different MnOx catalysts calculated by the BJH method (<a class="ext-link" href="/doi/suppl/10.1021/acs.langmuir.0c02841/suppl_file/la0c02841_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Manganese oxide octahedral molecular sieves: preparation, characterization, and applications

A Facile Template-Free Preparation of Porous Manganese Oxides by Thermal Decomposition Method

Synthesis, Characterization and Catalytic Combustion Properties of Manganese Oxide Octahedral Molecular Sieve

An ultrasonic atomization assisted synthesis of self-assembled manganese oxide octahedral molecular sieve nanostructures and their application in catalysis and water treatment.

Ionic Liquids Assisted Preparation of Manganese Dioxide and Its Catalytic Properties

Large-Scale Preparation of Hierarchical Manganese Oxide Octahedral Molecular Sieves (Oms-1) Composed of Nanoplate Microspheres Via A Facile One-Pot Reflux Method

Water Oxidation Catalysis by Synthetic Manganese Oxides with Different Structural Motifs: A Comparative Study

Microscale Mn2O3 Hollow Structures: Sphere, Cube, Ellipsoid, Dumbbell, and Their Phenol Adsorption Properties

Synthesis of Perforated Single-Crystalline Mn2O3 Microcubes for Thermocatalytic Applications†

Controlled Synthesis, Characterization, And Catalytic Properties Of Mn2o3 And Mn3o4 Nanoparticles Supported On Mesoporous Silica Sba-15

Synthesis and adsorption properties of metal oxide-coated lithium ion-sieve from salt lake brine

Significant Enhancement of Catalytic Activities of Manganese Oxide Octahedral Molecular Sieve by Marginal Amount of Doping Vanadium

Synthesis of Large Mesoporous-Macroporous and High Pore Volume, Mixed Crystallographic Phase Manganese Oxide, Mn2O3/Mn3O4 Sponge

Mesoporous manganese dioxide prepared by nano-casting: An efficient catalyst for of methyl orange and oxalic acid degradation in aqueous solution

Atomic Mechanisms of Cation Adsorption/Exchange in Octahedral Molecular Sieves

Insights into the Reactive and Deactivation Mechanisms of Manganese Oxides for Ozone Elimination: The Roles of Surface Oxygen Species

Study on the mechanism of catalytic oxidative degradation of oxalic acid by two-dimensional (2D) shaped manganese dioxide

Electron Spin Resonance And Electron Spin Echo Modulation Spectroscopy Of Aluminophosphate-Based Mesoporous Molecular Sieve Containing Framework Manganese

Single Crystal Manganese Oxide Hexagonal Plates with Regulated Mesoporous Structures

Highly active OMS-2 for catalytic ozone decomposition under humid conditions

Synthesis and Catalytic Performance of Manganese Oxide Octahedral Molecular Sieve Nanorods for Formaldehyde Oxidation at Low Temperature