Abstract:Laser cladding, which is characterized by the minimal thermal impact on the substrate, is an advanced technique to restore the working dimensions of parts subject to wear. The Ni–Cr–B–Si system coatings can be used for parts operating at high temperatures. Our work aims at studying the effect of heating and subsequent cooling conditions in the process of high-temperature treatment on the features of the structural and phase state of the coating obtained by laser cladding of the PG-SR2 powder (chemical composition, wt %: 14.8 Cr, 2.1 B, 2.9 Si, 2.6 Fe, and 0.48 S; the rest is Ni) and the properties obtained as a result of this treatment (hardness and tribological characteristics in sliding on fixed abrasive corundum). Samples with a laser-clad layer were heated at a temperature of 1050°C (holding for 1 h) and subsequently cooled in water (which made it possible to record structural transformations under high-temperature heating), in air, and in a muffle and a vacuum furnace. It has been shown that the rate of cooling during the high-temperature treatment of the laser-clad PG-SR2 coating significantly affects the structure and properties. High-temperature heating leads to partial diffusive dissolution of nickel borides (Ni 3 B) and chromium carbides (Cr 23 C 6 ) in a solid solution and a corresponding decrease in hardness and an increase in the abrasive wear intensity and the coefficient of friction. The reduction in the rate of cooling from 1050°C of the samples in air, a muffle furnace, or a vacuum furnace leads to the precipitation of chromium borides (CrB) and nickel silicide (Ni 3 Si), which were absent in the clad coating structure. High-strength CrB borides whose hardness is equal to or even exceeds that corundum abrasive hinder the development of the microcutting mechanism in the process of abrasive wear. Coarse chromium carbides and borides formed in the process of slow cooling in the furnace form wear-resistant framelike structures. This results in an increase in hardness and abrasive wear resistance to the values that exceed those of the original clad coating.

Laser cladding of turbine blades

Laser cladding of aerospace materials

Research of Laser Cladding Coating on Turbine Blade Tip

Application of Laser Cladding Technology to Improve the Interface of Thermal Barrier Coatings

STUDY OF LASER CLADDING OF COMPOSITE COATINGS

Laser Surface Cladding: the State of the Art and Challenges

Experimental Study of Laser Cladding Methods on Water Erosion Resistance to Low Pressure Blades Materials of Steam Turbine

Preparation and the Mechanical and Tribological Properties of Laser Cladding Coating

Study of Microstructure and Properties of Laser Cladding Ni60-WC + TiC Composite Coating

A comparative study on microstructure and properties of Inconel 52M overlays deposited by laser beam and GTA cladding

Effect of WC on Microstructure and Wear Resistance of Fe-Based Coating Fabricated by Laser Cladding

Microstructural Characterization of Thermal Barrier Coatings Glazed by a High Power Laser

Effect of Conditions of High-Temperature Treatment on the Structure and Tribological Properties of Nickel-Based Laser-Clad Coating

A comparative study on characteristics of composite (Cr3C2-NiCr) clad developed through diode laser and microwave energy

A contribution to laser cladding of Ti-6Al-4V titanium alloy

Laser Cladding of Electroplated Ni-WC on Surface of TA2:microstructure and Mechanical Properties

Study on fabrication of multi-phase reinforcement coatings on Ti6Al4V by laser cladding for enhanced tribological performance

Effect of laser remelting on the tribological performance of thermal barrier coatings

Laser Cladding of TiC for Better Titanium Components

Improved High-Temperature Hardness and Wear Resistance of Inconel 625 Coatings Fabricated by Laser Cladding

Effect of Deep Cryogenic Treatment on Microstructure and Wear Resistance of LC3530 Fe-Based Laser Cladding Coating