Structural and Mossbauer studies of ball milled Co-Zn Y-type hexaferrites

M.A. Awawdeh,R.N. Al-Bashaireh,A-F. Lehlooh,S.H. Mahmood

DOI: https://doi.org/10.48550/arXiv.1707.09122

2017-07-28

Abstract:Y-type hexaferrite samples Ba2ZnxCo2-xFe12O22 with x = 0, 1 and 2 were prepared from precursors synthesized by the citrate sol-gel auto combustion method. The powders were sintered at 1100° C for four hours. X-ray diffraction, scanning electron microscopy and Mössbauer spectroscopy were used to investigate the effect of ball milling on the structure, microstructure and on the hyperfine parameters. X-ray diffraction revealed the presence of a single Y-type hexaferrite in all sintered samples. This phase persisted in samples milled for periods up to four hours. Scanning electron microscopy images indicated that the particles changed shape, and their sizes reduced by a factor of 10 for milling times of four hours. Room temperature Mössbauer spectra of the hexaferrites elucidated the distribution of the various cations at the various sites of the hexaferrite lattice. The hyperfine field (Bhf) associated with each component was found to decrease almost exponentially with increasing milling time. The reduction in hyperfine field was associated with the weakening of the superexchange interactions between the spin-up and spin-down sublattices as a consequence of replacing Co2+ magnetic ions by non-magnetic Zn2+ ions and with the microstructure in the milled samples.

Materials Science

What problem does this paper attempt to address?

This paper aims to study the influence of ball - milling treatment on the structure, microstructure and hyperfine parameters of cobalt - zinc Y - type hexagonal ferrite (Ba_2Zn_xCo_{2 - x}Fe_{12}O_{22}, x = 0, 1, 2). Specifically, the paper uses methods such as X - ray diffraction (XRD), scanning electron microscopy (SEM) and Mössbauer spectroscopy to explore the changes in the crystal structure, particle size and hyperfine field of samples under different ball - milling times.

### Main research questions:
1. **Structural stability**: Will ball - milling treatment lead to phase transformation or structural change of Y - type hexagonal ferrite?
2. **Microstructural change**: What is the impact of ball - milling treatment on the particle morphology and size of the sample?
3. **Hyperfine parameter change**: What is the impact of ball - milling treatment on the hyperfine field (B_hf) of the sample? In particular, what is the change trend of the hyperfine field as the ball - milling time increases?

### Research methods:
- **Sample preparation**: Prepare the precursor by the citric acid sol - gel self - combustion method and sinter it at 1100°C for 4 hours.
- **Ball - milling treatment**: Use a planetary ball mill to perform ball - milling treatment on the sample for different times.
- **Characterization means**:
- **X - ray diffraction (XRD)**: Analyze the crystal structure and grain size of the sample.
- **Scanning electron microscopy (SEM)**: Observe the microscopic morphology and particle size of the sample.
- **Mössbauer spectroscopy**: Study the hyperfine parameters of the sample, such as hyperfine field (B_hf) and center shift (CS).

### Key findings:
- **Structural stability**: XRD results show that even after up to 8 hours of ball - milling treatment, the sample still maintains a single Y - type hexagonal ferrite phase.
- **Microstructural change**: SEM images show that ball - milling treatment changes the particles from flake - like to approximately spherical, and the particle size is significantly reduced, with the maximum reduction to one - tenth of the original size.
- **Hyperfine parameter change**: Mössbauer spectroscopy results indicate that as the ball - milling time increases, the hyperfine field (B_hf) gradually decreases, which is related to the substitution of Co^2+ magnetic ions by non - magnetic Zn^2+ ions and also related to the microstructural change of the sample.

### Conclusion:
Ball - milling treatment has a relatively small impact on the structural stability of cobalt - zinc Y - type hexagonal ferrite, but significantly changes its microstructure and hyperfine parameters. These changes are of great significance for understanding the magnetic properties of materials and their potential applications.