Thermal analysis and SANS characterisation of hybrid materials for biomedical applications

J.J.H. Lancastre,F.M.A. Margaça,L.M. Ferreira,A.N. Falcão,I.M. Miranda Salvado,M.S.M.S. Nabiça,M.H.V. Fernandes,L. Almásy

DOI: https://doi.org/10.1007/s10973-011-1459-z

2017-02-02

Abstract:Silicate hybrid materials were prepared by the sol-gel process with the addition of x wt% of zirconium propoxide (x = 0 and 1). The thermal behavior as well as the influence of Zr addition was studied by thermal gravimetric analysis and differential thermal analysis. The microstructure evolution with temperature was investigated by X-ray diffraction and small angle neutron scattering. It was found that the beginning of polymer degradation occurs at a higher temperature in the material prepared with addition of Zr than in the one prepared without. At the nanometric scale, the materials prepared without Zr show smooth interfaces, whereas those with Zr present a mass fractal structure. This structure is also observed in the material without Zr after thermal treatment at 200 C. The results showed that bioactivity is favored by mass fractal structures in comparison with one consisting of smooth surfaces.

Materials Science

What problem does this paper attempt to address?

The problem this paper attempts to address is: studying the thermal behavior, microstructure, and their effects on the bioactivity of silicate hybrid materials containing different proportions of zirconium (Zr) for biomedical applications.

Specifically, the authors prepared silicate hybrid materials containing different proportions of zirconium using the sol-gel method and conducted the following studies:
1. **Thermal Behavior Analysis**: Investigated the thermal stability of the materials through thermogravimetric analysis (TGA) and differential thermal analysis (DTA).
2. **Microstructure Characterization**: Studied the microstructural changes of the materials at different temperatures using X-ray diffraction (XRD) and small-angle neutron scattering (SANS) techniques.
3. **Bioactivity Evaluation**: Assessed the bioactivity of the materials by immersing them in simulated body fluid (SBF), particularly focusing on the deposition of the hydroxyapatite (HA) layer.

The main findings include:
- Materials with added zirconium (Zr) exhibit higher thermal stability at high temperatures.
- Materials without zirconium present a smooth interface after drying, while those with zirconium show a mass fractal structure.
- After heat treatment, materials without zirconium also display a mass fractal structure.
- Materials with a mass fractal structure are more likely to promote the deposition of hydroxyapatite, thus exhibiting better bioactivity compared to materials with a smooth surface.

These results help to understand the role of zirconium in hybrid materials and how to enhance their bioactivity by adjusting the nanostructure of the materials, providing important scientific evidence for the development of new biomedical materials.