Interfacial microstructure and mechanical properties of WC–Co/40Cr joints brazed at low–temperature with Ag–Cu–Ti + Sn novel filler
Zhaoyang Zheng,Minyun Xu,Shaoheng Wang,Ruina Ma,Ruina Ma,An Du,An Du,Yongzhe Fan,Yongzhe Fan,Xue Zhao,Xue Zhao,Xiaoming Cao,Xiaoming Cao
DOI: https://doi.org/10.1016/j.vacuum.2023.111988
IF: 4
2023-06-01
Vacuum
Abstract:It is crucial to design a novel active filler metal for brazing WC–Co cemented carbide–steel joints at low temperatures. In this study, we designed a low-melting-point multi-component active filler metal (Ag–Cu–Sn–Ti) based on Ag–Cu–Ti filler metal to achieve perfect combination of WC–Co/40Cr steel joints. The interfacial microstructure of the WC–Co/40Cr steel joint was comprehensively characterized, and the joint-bonding mechanism, mechanical properties, and fracture behavior after brazing at 700–780 °C were systematically analyzed. On both sides of the filler metal, WC and α-Fe combined with the TiC layer, enhancing the bonding of the filler metal to base materials. The typical structure of the joint is WC–Co/TiC layer/Co2SnTi + Cu–doped Cu81Sn22 + Ag [s, s] + Ti–Cu granules/TiC layer/40Cr. The maximum shear strength of 241 MPa was obtained when the joint was brazed at 740 °C for 10 min, which is approximately 50% higher than those of previous low-temperature vacuum-brazed WC–Co/steel joints. The main factors leading to premature failure of joint include the distribution of phases in filler metal layer and defects of WC–Co caused by Co diffusion.
materials science, multidisciplinary,physics, applied