Two parameter characterization of semi-circular cracks in anisotropic plastic materials

Arnav Rana,Ronald E. Miller,Xin Wang

DOI: https://doi.org/10.1016/j.engfracmech.2024.109954

IF: 5.4

2024-02-13

Engineering Fracture Mechanics

Abstract:In this paper, the J - Q two-parameter characterization of Hill-anisotropic elastic–plastic crack-front fields are examined for surface cracked plates under uniaxial tensile loadings. A method for two-parameter characterization crack-front field in anisotropic plastic materials is presented. Extensive three-dimensional elastic–plastic finite element analyses were performed for semi-circular surface cracks in a finite thickness plate, under remote uniaxial tension loading conditions. Surface cracks with relative depths a/t = 0.2, 0.6 were investigated. The loading levels spanned from small-scale to large-scale yielding. Different crack orientations with respect to the material coordinate directions were also considered. In topological planes perpendicular to the crack front, the crack-front stress fields were obtained. In order to facilitate the determination of Q -factors, modified boundary layer analyses were also conducted. The modified boundary layer analyses were adapted to account for plastic anisotropy. The J - Q two-parameter approach was then used in characterizing the elastic–plastic crack-front stress fields along these 3D crack fronts. Complete distributions of the J -integral and Q -factors for a wide range of loading conditions were obtained. The results indicate that the J – Q characterization is applicable to Hill-anisotropic plastic materials and provides good estimate for the crack-front constraint loss experienced under large-scale yielding. It was also observed that the isotropic and anisotropic J – Q parameters can significantly diverge, especially, when crack planes are misaligned with respect to the material coordinate system. This highlights the importance of the consideration of plastic anisotropy when performing constraint-based fracture mechanics analyses.

mechanics