Synthesis and characterization of high‐sensitivity Dy,Eu co‐doped CaSO4 thermoluminescent phosphor using coprecipitation technique

Salwa Mohamed,Elsayed Salama,Huda A. Alazab,Assem Bakry,Archana Sharma,Yasser Assran

DOI: https://doi.org/10.1002/bio.4679

IF: 2.613

2024-01-21

Luminescence

Abstract:In this work (99 − x)Ca2SO4‐Dy2O3–xEu2O3, (x = 0, 0.05, 0.1, 0.2, 0.3, 0.4, 0.5) thermoluminescence phosphors are prepared using the coprecipitation method. The obtained results showed that the most sensitive phosphor was obtained at x = 0.05. Despite the phosphor's high fading rate of 71% after 1 month, the batch sensitivity of the prepared samples was ~90% compared with TLD‐100. These findings suggest that the synthesized phosphor is well suited for applications involving low‐dose radiation dosimetry. In this work, (99 − x)CaSO4‐Dy2O3–xEu2O3, (where x = 0, 0.05, 0.1, 0.2, 0.3, 0.4, 0.5) thermoluminescence phosphors were prepared using a coprecipitation method. The thermoluminescence (TL) dosimetry (TLD) characteristics such as TL sensitivity, dose–response, minimum detectable dose, thermal fading, and the effect of sunlight on the prepared phosphors were investigated. The obtained results indicated that the most sensitive phosphor was obtained at x = 0.05. Large thermal fading of 6% after 1 h and 26% after 24 h from irradiation followed by 71% after 1 month with no additional fading was observed within a time frame exceeding 2 months throughout the remaining duration of the investigation, which also spanned over 2 months. Despite the phosphor's high fading rate, the relative sensitivity of the prepared samples was ~90% compared with TLD‐100. The marked effect of day sunlight was also determined. High dose–response within the low‐dose range from 0.01 to 5 Gy was observed. The obtained results suggested that the synthesized phosphor is well suited for applications involving radiation biology and radiotherapy dosimetry.

chemistry, analytical