Unconventional dual-vacancies in nickel diselenide-graphene nanocomposite for high-efficiency oxygen evolution catalysis

Pengkun Wei,Zewei Hao,Yang Yang,Mingyang Liu,Haijun Zhang,Min-Rui Gao,Shu-Hong Yu
DOI: https://doi.org/10.1007/s12274-020-3005-4
IF: 9.9
2020-08-22
Nano Research
Abstract:<p class="a-plus-plus">Although nickel-based catalysts display good catalytic capability and excellent corrosion resistance under alkaline electrolytes for water splitting, it is still imperative to enhance their activity for real device applications. Herein, we decorated Ni<sub class="a-plus-plus">0.85</sub>Se hollow nanospheres onto reduced graphene oxide (RGO) through a hydrothermal route, then annealed this composite at different temperatures (400 °C, NiSe<sub class="a-plus-plus">2</sub>-400 and 450 °C, NiSe<sub class="a-plus-plus">2</sub>-450) under argon atmosphere, yielding a kind of NiSe<sub class="a-plus-plus">2</sub>/RGO composite catalysts. Positron annihilation spectra revealed two types of vacancies formed in this composite catalyst. We found that the NiSe<sub class="a-plus-plus">2</sub>-400 catalyst with dual Ni-Se vacancies is able to catalyze the oxygen evolution reaction (OER) efficiently, needing a mere 241 mV overpotential at 10 mA·cm<sup class="a-plus-plus">−2</sup>. In addition, this catalyst exhibits outstanding stability. Computational studies show favorable energy barrier on NiSe<sub class="a-plus-plus">2</sub>-400, enabling moderate OH<sup class="a-plus-plus">−</sup> adsorption and O<sub class="a-plus-plus">2</sub> desorption, which leads to the enhanced energetics for OER. </p>
materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology
What problem does this paper attempt to address?