Abstract:We consider the classical problem of the stick-slip dynamics observed when peeling a roller adhesive tape at a constant velocity. From fast imaging recordings, we extract the dependencies of the stick and slip phases durations with the imposed peeling velocity and peeled ribbon length. Predictions of Maugis and Barquins [in Adhesion 12, edited by K.W. Allen, Elsevier ASP, London, 1988, pp. 205--222] based on a quasistatic assumption succeed to describe quantitatively our measurements of the stick phase duration. Such model however fails to predict the full stick-slip cycle duration, revealing strong dynamical effects during the slip phase.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is the "stick - slip" dynamic phenomenon observed during the process of peeling off the adhesive tape at a constant speed. Specifically, through high - speed imaging records, the author extracted the relationships between the durations of the stick and slip phases and the applied peeling speed and the length of the peeled - off tape. The research aims to verify whether the prediction model based on the quasi - static assumption by Maugin and Barquins can quantitatively describe the measured duration of the stick phase, and to explore the limitations of this model in predicting the duration of the entire stick - slip cycle, and to reveal the strong dynamic effects in the slip phase.
### Research Background
In daily life, during the peeling process of adhesive tapes (such as labels, stamps, tape rolls, self - adhesive envelopes or sticky notes), a dynamic instability called "stick - slip" may occur. This instability will cause the sudden advancement of the peeling front, generate noise, damage the adhesive layer, and even lead to mechanical problems on the assembly line. Since the 1950s, this instability has been an industrial concern because the noise level it generates exceeds the work regulation limits and may lead to mechanical failures. Although there are currently some general - purpose technical solutions (such as anti - stick silicone coatings) to suppress this instability, their effects are limited and it is still an important factor affecting industrial productivity.
From the perspective of fundamental research, the "stick - slip" instability is generally considered to be caused by the abnormal decrease of the fracture energy \(\Gamma(v_p)\) of the adhesive - substrate joint within a specific range of the peeling speed \(v_p\). When the peeling process also involves the flexibility between the point where the peeling speed is applied and the fracture front, this decreased fracture energy will naturally lead to the oscillation of the fracture speed \(v_p\) around the average speed \(V\) applied by the operator. Usually, only the elasticity of the peeled - off tape provides the flexibility of the system. From a microscopic perspective, this abnormal decrease of the fracture energy may correspond to the transition from cohesive failure to adhesive failure, or the transition between two different interface failure modes. More fundamentally, this decrease of the fracture energy is considered to be caused by the viscous dissipation in the adhesive material. De Gennes further pointed out that the limitation of the adhesive material may be a fundamental factor in this viscoelastic theory.
### Experimental Method
In the experiment, a high - speed camera was used to shoot the local dynamics of the peeling point at a speed of 20,000 frames per second. Through direct image analysis, the curvature position \(\ell_\alpha(t)=R\alpha\) (where \(\alpha\) is the angular position of the peeling point and \(R\) is the diameter of the drum) of the peeling point in the laboratory frame can be obtained. Through the image correlation processing of the contrast pattern of the adhesive tape drum, its angular velocity \(\frac{d\beta}{dt}(t)\) (where \(\beta\) is the angular position of the drum unrolling) in the laboratory frame can be directly obtained. Finally, through numerical calculation, the curvature position \(\ell_p(t)=\ell_\beta(t)+\ell_\alpha(t)\) and the speed \(v_p(t)=\frac{d\ell_p}{dt}\) of the peeling point in the drum reference frame are obtained.
### Main Findings
- **Stick - Slip Amplitude and Period**: For each stick - slip event, the peeling amplitude \(A_{ss}\) and the corresponding stick - slip period \(T_{ss}\) show a relationship close to \(A_{ss} = VT_{ss}\). This indicates that, on average statistically, \(A_{ss}\) and \(T_{ss}\) increase as the length \(L\) of the peeled - off tape increases.
- **Durations of Stick and Slip Phases**: The duration \(T_{stick}\) of the stick phase is almost proportional to the length \(L\) of the peeled - off tape and decreases as the peeling speed \(V\) increases; while the duration \(T_{slip}\) of the slip phase increases as \(V\) increases within the entire explored speed range. Therefore, the ratio \(T_{stick}/T_{slip}\) decreases as \(V\) increases, from about \(4\pm1\) to about \(0.3\pm0.2\).
- **Model Verification**: The model proposed by Barquins, Maugis and their colleagues is consistent with the experimental data at low peeling speeds, but at high peeling speeds, the slip - phase duration predicted by the model is much smaller than the experimental value. This indicates that there are strong dynamic effects in the slip phase.