Anamolous reduction of magnetic coercivity of graphene oxide and reduced graphene oxide upon cooling

K. Bagani,A. Bhattacharya,J. Kaur,A. Rai Chowdhury,B. Ghosh,M. Sardar,S. Banerjee

DOI: https://doi.org/10.1063/1.4861173

2013-02-14

Abstract:In this report we present the temperature evolution of magnetic coercivity of graphene oxide (GO) and reduced graphene oxide (RGO). We report an anamolous decrease in coercivity of GO and RGO with decreasing temperature. We could explain this anamolous behavior invoking the inherent presence of ripple in graphene. We observe antiferromagnetic and ferromagnetic behavior at room temperature for GO and RGO respectively, but at low temperatures both shows paramagnetic behavior.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: **The abnormal decrease in magnetic coercivity during the cooling process of graphene oxide (GO) and reduced graphene oxide (RGO)**.

Specifically, the authors studied the magnetic behavior of GO and RGO as a function of temperature and found that as the temperature decreased, the magnetic coercivity of these two materials decreased instead. This phenomenon is contrary to the usually expected trend of coercivity increasing as the temperature decreases. To understand this anomalous behavior, the authors proposed a possible explanation, that is, the inherent ripple structure in graphene has an impact on magnetism.

### Research Background

1. **Magnetism of Graphene and Its Derivatives**:
- Graphene and its derivatives such as GO and RGO exhibit unique magnetism, which is related to defects, topological structures, and functional groups in the materials.
- For example, graphene oxide (GO) exhibits antiferromagnetism and ferromagnetism at room temperature, while reduced graphene oxide (RGO) exhibits ferromagnetism.

2. **Experimentally Observed Phenomena**:
- At high temperatures, both GO and RGO exhibit hysteresis loops, but as the temperature decreases, the hysteresis loops gradually disappear.
- At low temperatures (such as 10K), the hysteresis loops of the two materials almost disappear, showing paramagnetic behavior.

### Explanation and Discussion

1. **Influence of Ripple Structure**:
- The authors believe that the ripple structure in graphene will cause changes in the local magnetic anisotropy energy.
- As the temperature decreases, the ripple structure becomes more obvious, resulting in a decrease in the average magnetic anisotropy energy, thereby reducing the coercivity.

2. **Source of Magnetic Moments**:
- The magnetic moments in GO and RGO mainly come from defects and functional groups (such as hydroxyl groups, epoxy groups, etc.) in the materials. The presence of these groups will destroy the planar structure of graphene, resulting in the generation of local magnetic moments.
- The reduction process will remove some functional groups and reduce defects, so the magnetic moment of RGO is smaller than that of GO.

3. **Relationship between Magnetic Anisotropy Energy and Coercivity**:
- The relationship between coercivity and magnetic anisotropy energy density \(K\) and saturation magnetization \(M_s\) is:
\[
H_c\propto\frac{K}{M_s}
\]
- Since the structure of GO is more disordered, its magnetic anisotropy energy density \(K\) is smaller, so the coercivity is lower; while the structure of RGO is more regular, the magnetic anisotropy energy density is higher, and the coercivity is larger.

### Conclusion

Through experimental and theoretical analysis, the authors explained the abnormal decrease in magnetic coercivity of GO and RGO during the cooling process and attributed it to the influence of the ripple structure in the materials on the magnetic anisotropy energy. This research is helpful for in - depth understanding of the magnetic behavior of graphene and its derivatives and provides a theoretical basis for further development of graphene - based magnetic materials.