Synthesis of reduced graphene oxide quantum dots from graphene oxide via hydrothermal process and theirs structural, luminescence and magnetic properties
Nattha Buatong,Chesta Ruttanapun,Chaval Sriwong
DOI: https://doi.org/10.1016/j.jtice.2022.104667
IF: 5.477
2023-01-12
Journal of the Taiwan Institute of Chemical Engineers
Abstract:Highlights • The GQDs were synthesized by hydrothermal process. • The blue photoluminescence GQDs was directly related to the presence of aromatic sp 2 conjugated structure, emissive free zigzag sites and quantum size effect. • Unpaired electron was observed by EPR in the GQDs as a function of hydrothermal reduction temperature. • The GQDs showed the crossover between paramagnetic and diamagnetic with the residual edge states and morphological change. Background Reduced graphene oxide quantum dots (rGO-QDs) have attracted much interest because of its exceptional chemical and physical properties and novel applications in a new technology and devices such as, energy storage, electrochemical, photocatalysis, sensing, drug delivery, bioimaging and anticancer therapy. Methods In this work, we reported a correlation study of the structural, morphological, luminescence and magnetic behavior of rGO-QDs as a function of hydrothermal reduction temperatures (such as 90 °C, 120 °C, 150 °C and 180 °C) of GO sheets precursor via hydrothermal process. GO precursor and the obtained rGO-QDs samples were confirmed and analyzed by several techniques such as, XRD, Raman, XPS, TEM, PL, UV–Visible, Fluorescence and EPR. Significant findings Influence of hydrothermal cutting process with different temperatures (90 °C, 120 °C, 150 °C and 180 °C) on the evolution of structural, morphologies, luminescence and magnetic behavior for the changes of large GO sheets into ultra-small rGO-QDs is presented. XRD result confirmed the effect of increasing temperature on the hydrothermal cutting process which led to a decrease in d -spacing values of rGO-QDs products. While Raman results indicates the trend of I D /I G ratio decreases along with increasing hydrothermal reduction temperatures. XRS analysis revealed that the percentage of carbon content of GO precursor (∼64%) was shifted value to ∼83% for obtained rGO-QDs sample prepared at 180 °C. TEM images shown that a very thin plate-like shape with ultrasmall average diameter of rGO-QDs samples in rage of 22±2 nm to 8 ± 2 nm. The optical and PL results well-confirmed the characteristic quantum size effect of all rGO-QDs samples. Finally, the EPR signals indicate the crossover between paramagnetic and diamagnetic are depended on the reduction temperature. The rGO-QDs prepared at 180 °C do not give any EPR signal, signify the nonmagnetic nature. This indicate that the basal plane of rGO-QDs at 180 °C has nearly perfect sp 2 network of graphene. Graphical abstract Download : Download high-res image (146KB) Download : Download full-size image
engineering, chemical