Mesoscopic Influence Mechanism of Particle Fragmentation on Compressive Deformation of Gangue Aggregates with Different Gradations under Load
Laiwei Wu,Junmeng Li,Yanli Huang,Peng Huang,Changde Yang,Zizhao Ding,Hong Yu
DOI: https://doi.org/10.1016/j.mineng.2024.108893
IF: 5.479
2024-01-01
Minerals Engineering
Abstract:The crushing and deformation behavior of gangue aggregate is a key factor affecting the stability of the overburden in goaf, and the particle size gradation has a significant impact on the particle fragmentation and compressive deformation of gangue aggregate. In this study, compression tests on crushed gangue aggregates with different particle size gradations were conducted, and the fragmentation of gangue was quantitatively characterized by using fractal dimension. Additionally, a lateral confined compression particle flow model for gangue was established, the meso-structural evolution law of gangue aggregates under triaxial compression under different gradation conditions was studied, and the influence mechanism of the internal microstructure of crushed gangue on its macroscopic deformation was revealed. The research results indicate that: (1) the larger the Talbot coefficient n, the higher the gangue fragmentation rate and the larger the sample deformation. The deformation of the gangue sample primarily results from the compaction of voids and the fragmentation of the block. Void deformation mainly occurs in the early loading stage, and deformation amount of the gangue sample caused by void compaction accounts for about 60 %. The fragmentation deformation runs through the entire loading process, and the deformation amount of the gangue sample caused by block fragmentation accounts for about 40 %. (2) There is a good linear regression relationship between the fractal dimension n and the fragmentation rate, and the larger the initial gradation, the smaller the fractal dimension. During the loading process of the sample, large particle size gangue is mainly subject to fragmentation, while small particle size gangue mainly fills the gaps. Moreover, small particle size gangue can effectively weaken the stress concentration effect. (3) As the axial stress increases, the failure mode changes from tensile failure to shear failure, and the block contact mode gradually changes from point contact to surface contact. The stress-bearing zone extends from the top to the entire specimen, and the contact force chain between the gangue changes from circular to cylindrical shape, and the force chain gradually becomes directional. (4) The energy generation mainly comes from the friction and fragmentation between gangue blocks, and the strain energy generated by fragmentation is dominant. The variation of total energy can be divided into three stages: gradual increase stage, sharp increase stage, and stable stage.