Evolution of Magnetic Glass on Partial Crystallization of a Bulk Metallic Glass: Tb36Sm20Al24Co20

Archana Lakhani,A. Banerjee,P. Chaddah,J. Q. Wang,W. H. Wang

DOI: https://doi.org/10.48550/arXiv.1201.5255

2012-01-25

Abstract:A comparative study on as cast and annealed rare earth bulk metallic glass (BMG) with composition Tb36Sm20Al24Co20 has been carried out by magnetization measurements. The as cast amorphous sample shows non-ergodic magnetization but does not show the behavior expected from magnetic glass. After annealing, the partially crystallized BMG shows this magnetic glass behavior. This is confirmed by the established measurement protocol of cooling and heating in unequal fields (CHUF).

Materials Science,Strongly Correlated Electrons

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explore whether the rare - earth - based bulk metallic glass (BMG) with specific components can exhibit the behavior of magnetic glass after partial crystallization. Specifically, the research object is the material Tb₃₆Sm₂₀Al₂₄Co₂₀.

### Research Background and Problem Description

1. **Basic Characteristics of Bulk Metallic Glass (BMG)**
- Metallic glass is an amorphous material with disordered atomic arrangement and no periodic structure of crystals.
- Compared with ordinary metals, BMG has a higher requirement for cooling rate, but once formed, a larger sample size can be obtained.

2. **Magnetic Glass Behavior**
- Magnetic glass is a special magnetic material, and its magnetic moment exhibits non - ergodic behavior at low temperatures, that is, the magnetic moment cannot freely respond to the change of the applied magnetic field.
- This behavior can be confirmed by cooling and heating in unequal fields measurement (CHUF protocol).

3. **Research Purposes**
- To explore the differences in magnetic behavior of the rare - earth - based bulk metallic glass Tb₃₆Sm₂₀Al₂₄Co₂₀ in the as - cast and annealed states.
- Pay special attention to whether the partially crystallized BMG exhibits the characteristics of magnetic glass after annealing treatment.

### Experimental Methods and Results

1. **Preparation of Experimental Samples**
- The as - cast samples were formed by arc melting and suction casting in an argon atmosphere.
- The annealed samples were partially crystallized by annealing treatment at 450°C.

2. **Magnetic Measurement**
- Zero - field - cooling (ZFC) and field - cooling (FC) magnetization measurements were carried out at different magnetic field intensities using a vibrating sample magnetometer (VSM).
- The magnetic glass behavior of the annealed samples was further verified by the CHUF protocol.

3. **Main Findings**
- **As - cast Samples**: They exhibited non - ergodic magnetization behavior, but were insufficient in terms of the expected magnetic glass behavior.
- **Annealed Samples**: After partial crystallization, they showed typical magnetic glass behavior, including two magnetization jumps and non - ergodicity at low temperatures.

### Conclusion

This research shows that Tb₃₆Sm₂₀Al₂₄Co₂₀ does not have the characteristics of magnetic glass in the as - cast state, but does exhibit the behavior of magnetic glass after annealing treatment and partial crystallization. This finding provides an important basis for further understanding the magnetic transition mechanism of rare - earth - based bulk metallic glasses.

### Explanation of Formulas and Charts

The main formulas and charts involved in the paper are used to show the relationship between magnetization and temperature change, for example:

- \( \Delta M = M_{\text{ZFC}}(T) - M_{\text{FC}}(T) \) represents thermomagnetic irreversibility.
- Figure 1 and Figure 2 show the ZFC and FC magnetization curves at different magnetic fields and the magnetization - temperature dependence under the CHUF protocol.

These data and charts intuitively show the differences in magnetic behavior between the as - cast and annealed samples.