Abstract:Advances in Mechanical Engineering, Volume 14, Issue 8, August 2022. Five series of specimens with two different print orientations (−45/45 and 0/90) and two print layer thicknesses (0.1 and 0.2 mm) were made. In total 60 specimens with 100% filament infill were made. One specimen series (20 pieces) was isolated as a reference or thermally untreated. Before the thermal treatment (annealing), two specimen moulding methods were used: NaCl powder (granulation 63 mm: 20 pieces) and Calcium Sulphate (Gypsum: 20 pieces). During the annealing, specimens immersed in NaCl powder were heated in a drying oven to the filament melting point (for PLA: 200°C, with a duration interval of 30 min), while the treatment of the heated specimens in gypsum was performed at a temperature of around 190°C, with duration interval of 3 h with the observed temperature inside the mould of about 100°C. An ultrasonic bath and a drying oven were used in the gypsum treatment. Temperature measurement and control during both annealing treatments were performed using a thermal imaging camera, while the temperature control inside the drying oven was performed using a digital thermometer. After treatment, the specimens in the moulds were cooled at room temperature, and the dimensions of annealing and untreated specimens were controlled. Surface morphology was characterised using scanning electron microscopy (SEM). The SEM analysis reveals improved internal structure after heat treatment of the PLA specimens. These results show that the investigated specimens after heat treatments had better structural properties than the referent specimens. Tensile testing on a universal testing machine in compliance with the ASTM D638 standard was also performed. The referent PLA specimen with −45/45 and layer thickness of 0.1 mm had the highest tensile stress value (64.08 MPa) while the specimen with minimal tensile stress value before fracture was 0/90, 0.2 mm (54.81 MPa). Heat treatment in gypsum showed the most significant increase in strength with −45/45 (0.1 mm) being the strongest (71.66 MPa) while the strongest specimen treated in sodium chloride was −45/45 (0.1 mm) with maximum tensile stress of 70.08 MPa. The mechanical characteristics of the PLA were characterised using the Vickers microhardness tester. The PLA microhardness value was calculated according to standards ASTM E384 and ISO 6507. The referent PLA specimen with −45/45 (0.2 mm) orientation shows the maximal microhardness value (125 MPa), and the minimal microhardness value was observed for the 0/90 (0.1 mm) orientation specimens (108 MPa). The heat treatment specimens in gypsum have a better hardness (185 MPa) than those treated in gypsum (165 MPa), with microhardness increasing by about 12%. The essence of the work is reflected in the additional filament processing to achieve a better structural and mechanical performance of the materials and reduce the anisotropy that is characteristic of 3D printing.

Effects of annealing on the mechanical, thermal, and physical properties of 3D-printed PLA aged in salt water

Effects of annealing temperature and duration on mechanical properties of PLA plastics produced by 3D Printing

Impact of In-Soil Ageing Effect on PLA Printed Parts Tensile Properties

Effect of Thermal and Hydrothermal Accelerated Aging on 3D Printed Polylactic Acid

Accelerated ageing of polylactide in aqueous environments: Comparative study between distilled water and seawater

Enhancing mechanical properties of 3D printed thermoplastic polymers by annealing in moulds

Biodegradable materials with FDM technology under the aging effect of solar and saltwater exposure

Tailoring the Thermal and Mechanical Properties of Injection‐molded Poly (lactic Acid) Parts Through Annealing

High Pressure Salt Water and Low Temperature Effects on the Material Performance Characteristics of Additive Manufacturing Polymers

Investigating the Effects of Annealing on the Mechanical Properties of FFF-Printed Thermoplastics

Strengthening Polylactic Acid by Salification: Surface Characterization Study

Effect of Hydrothermal Aging on Injection Molded Short Jute Fiber Reinforced Poly(Lactic Acid) (PLA) Composites

Effect of Saline and Alkaline Solution Aging on the Properties of Jute/poly(lactic Acid) Composites

Improving Mechanical Properties for Extrusion-Based Additive Manufacturing of Poly(Lactic Acid) by Annealing and Blending with Poly(3-Hydroxybutyrate).

Effect of Aging on Tensile and Chemical Properties of Polylactic Acid and Polylactic Acid-Like Polymer Materials for Additive Manufacturing

Physical Aging and Glass Transition Dynamics of Semicrystalline Poly(lactic acid) for 3D-Printing Applications Investigated by Fast Scanning Calorimetry

Effects of Short-Term Thermal Aging on the Fracture Behavior of 3D-Printed Polymers

Effect of high pressure salt water absorption on the mechanical characteristics of additively manufactured polymers

Non-destructive Spectroscopic Diagnostic Tools for the Assessment of the Mechanical Strength of 3D-Printed PLA

Mechanical Properties of 3D Printed Parts and Their Injection Molded Alternatives Subjected to Environmental Aging

Heat‐Treatment and Water Immersion Effect on the Mechanical Properties and Joint Strength of 3D‐Printed Polylactic Acid Parts