Abstract:Objectives: The present study aimed to establish Lactobacillus casei in a completely automated Streptococcus mutans-based artificial mouth model and to investigate secondary caries inhibiting properties of glass ionomer cements / resin composite groups in vitro. Methods: Sixty extracted, caries-free human third molars were used for preparation of standardized class-V-cavities. Specimens were restored with a resin-modified (Photac Fil; PF) as well as a conventional glass ionomer cement (Ketac Molar; KM) and one resin composite bonded with and without conduction of etch-and-rinse technique (Prime&Bond NT, Ceram X mono; C+ERT, C). Following an incubation in distilled water for 28d at 37°C, specimens were exposed to 10,000 thermocycles (+5 °C/+55°C). A completely automated S. mutans-based (DSM No.: 20523) artificial mouth model was extended by establishment of L. casei (DSM No.: 20021). During microbiological loading, demineralization (4h/d) was caused by acid production resulting from bacterial glycolysis and artificial saliva was used for remineralization (20h/d). For quantitative margin analysis under am SEM, epoxy replicas were produced from impressions taken after thermocycling and after microbiological loading. Specimens were cut in half perpendicularly to restoration surfaces and demineralization depths at restoration margins and in 500μm distance from margins were evaluated by means of a fluorescence microscope (FITC filter). Results: After microbiological loading, overall demineralization depths in enamel at restoration margin (EM) and in 500μm distance (ED) as well as in cementum/dentin at restoration margin (DM) and in 500μm distance (DD) were measured as follows (μm±SD): PF: EM 42±15, ED 60±17, DM 83±18; DD 127±16; KM: EM 46±22, ED 62±17, DM 104±21, DD 143±28; C+ERT: EM 67±19, ED 61±17, DM 165±31, DD 176±35; C: EM 65±23, ED 64±17, DM 161±27, DD 166±33. For the glass ionomer cements, the overall demineralization depths at restoration margins were significantly lower than in 500μm distance from margins (T-test, p<0.05). Especially at restoration margins in cementum/dentin, the resin composite groups showed significantly larger overall demineralizations than the glass ionomer cements (ANOVA, mod. LSD, p<0.05). Decreases of marginal quality were detected in all groups after microbiological loading (Friedman-test, p<0.05). Significance: The refined experimental setup was suitable for production of artificial secondary caries-like lesions. Glass ionomer cements as fluoride-releasing materials may show an inhibition of secondary caries formation to a certain extent.

Effect of surface coating on water migration into resin-modified glass ionomer cements: a magnetic resonance micro-imaging study

Effect of a novel coating material on the microleakage of glass hybrid restoration in primary teeth – An in vitro study

Effect of various surface coating methods on surface roughness, micromorphological analysis and fluoride release from contemporary glass ionomer restorations

A Scanning Electron Microscope Evaluation of the Efficacy of Different Fluoride-releasing Dental Restorative Materials to Prevent Enamel Demineralization: An In Vitro Study

The influence of light‐curing time on fluoride release, surface topography, and bacterial adhesion in resin‐modified glass ionomer cements: AFM and SEM in vitro study

Glass-ionomer and calcium silicate-based cements interactions with human dentine in health and disease: Two-photon fluorescence microscopy and Raman spectroscopy analysis.

The effect of long-term water storage on the resin adhesive interface between dentine and glass ceramic

Effect of Resin Coating on Adhesion of Composite Crown Restoration

In vitro Study on Water Absorption of Dental Restorative Materials

A Repeated State of Acidification Enhances the Anticariogenic Biofilm Activity of Glass Ionomer Cement Containing Fluoro-Zinc-Silicate Fillers

Surface morphology and mechanical properties of conventional and self-adhesive resin cements after aqueous aging.

Secondary caries formation with a two-species biofilm artificial mouth

Environmental degradation of glass-ionomer cements: A depth-sensing microindentation study

Effect of Laser Irradiance and Fluoride Varnish on Demineralization Around Dental Composite Restorations

Elemental analysis and micromorphological patterns of tooth/restoration interface of three ion-releasing class V restorations

Noninvasive assessment of novel nanohybrid resin cement adaptation using cross-polarization optical coherence tomography

Enhancement of dentin bond strength of resin cement using new resin coating materials

Effect of silver diamine fluoride and ammonium hexafluorosilicate applications with and without Er:YAG laser irradiation on the microtensile bond strength in sound and caries-affected dentin

A Comparison of Laser and Mechanical Surface Pretreatment Methods on Shear Bond Strength of Resin Composite to Resin-Modified Glass Ionomer

Surface Degradation of Ion-releasing Restorative Materials With Cariogenic Challenge

Antibacterial and physical properties of resin cements containing MgO nanoparticles