Abstract:As the potential of using natural wood derivatives in the fabrication of composites is explored, it is important to gain further understanding of the structure and properties of wood cells. Past research has focused on estimating and measuring mechanical properties of wood cell walls such as hardness and modulus of elasticity by means of nano-indentation tests. However, to date, the mechanical properties of wood cell walls have not been fully understood or documented in the literature. The research described in this paper focuses, for the first time, on investigating the strength and fracture behavior of wood cell walls through an innovative approach, the uniaxial micro-compression test. Specimens of Keranji (Dialium ssp.), a dense Asian hardwood, and loblolly pine (Pinus taeda), an American softwood, were chosen as hardwood and softwood representatives for the micro-compression test. After the initial preparation by microtoming, the samples were further prepared following a novel approach, in which 37 cylindrical-shaped micro-pillars were fabricated using a Focused Ion Beam (FIB) with a voltage of 30kV, while each micropillar was milled inside a single wood cell wall. After the dimensions of each micropillar were measured by analysis of the SEM images using ImageJ software, a micro-compression test was conducted on the micropillar at a loading rate of 20nm per second using a Nano II Indenter system. The load–displacement curves were plotted, and the yield stress and compressive strength obtained for the Keranji cell wall were 136.5MPa and 160MPa, respectively; the yield stress and compressive strength of the loblolly pine cell wall were 111.3MPa and 125MPa, respectively. The fracture behavior of the wood micro-pillars confirmed the brittleness of the wood cell walls.

Structural and mechanical roles of wood polymer assemblies in softwood revealed by gradual removal of polysaccharides or lignin

Structure and Properties of Polymer Reinforced Wood-Based Composites

Wood-Polymer Composite Fabricated by Polymerization of Monomers Within Wood Porous Structure

Hemicellulose-rich Transparent Wood: Microstructure and Macroscopic Properties.

Wood Deformation Leads to Rearrangement of Molecules at the Nanoscale

Wood–polymer Composites Prepared by the in Situ Polymerization of Monomers Within Wood

Epoxy-Acrylic Polymer In-Situ Filling Cell Lumen and Bonding Cell Wall for Wood Reinforcement and Stabilization

Morphology, Mechanical Properties, and Dimensional Stability of Wood Particle/high Density Polyethylene Composites: Effect of Removal of Wood Cell Wall Composition

Effect of Polymer in Situ Synthesized from Methyl Methacrylate and Styrene on the Morphology, Thermal Behavior, and Durability of Wood

Preparation and property of wood polymer composite with a two-step method

Insights from Molecular Dynamics Simulations for Interfacial Effects Between Polylactic Acid and Wood Cell Wall Constituents

Towards high performance wood composites through interface customization with cellulose-based adhesive

Understanding the mechanical strength and dynamic structural changes of wood-based products using X-ray computed tomography

Solid Wood Modification toward Anisotropic Elastic and Insulative Foam-Like Materials

Wood-Polymer Composite Prepared by In Situ Synthesis of Copolymer within Wood and its Dimensional Stability

Structure-property relationship between lignin structures and properties of 3D-printed lignin composites

Thermoforming of Polymer from Monomers in Wood Porous Structure and Characterisation for Wood–polymer Composite

Characterizing strength and fracture of wood cell wall through uniaxial micro-compression test

Performance of wood-polymer composite prepared by in-situ synthesis of terpolymer within wood

Synthesis of biomass hyperbranched polyamide resin from cellulose and citric acid for wood adhesive

Contribution of lignin to the strength properties in wood fibres studied by dynamic FTIR spectroscopy and dynamic mechanical analysis (DMA)