Abstract:Four different thin film nanocomposite (TFN) membranes were prepared by adding different concentrations of porous Zr-MOFs (UiO-66 and UiO-66-NH2) to piperazine (PIP) aqueous solution (aqueous phase) or 1,3,5-Benzenetricarbonyl trichloride (TMC)-n-hexane solution (organic phase) by interfacial polymerization. The main purpose is to study the specific effects of different addition methods and addition amounts of nanoparticles on the structure and performance of the TFN membranes by interfacial polymerization. All four TFN membranes exhibited higher water permeability while maintaining high salt rejection compared to thin film composite (TFC) membrane. On the one hand, the TFN membranes behaves differently which are prepared by adding the same kind of nanoparticles to the aqueous phase or organic phase, respectively. The TFN membrane prepared by adding 0.2 w/v% UiO-66 to the organic phase had high water flux of 87.86 L·m-2·h-1, comparing 46.31 L·m-2·h-1 of membrane prepared by adding 0.3 w/v% UiO-66 in the aqueous phase. This is due to the fact that UiO-66 greatly slows the interfacial polymerization rate when UiO-66 is added to the organic phase, resulting in a thinner and more aperture polyamide thin film layer, reducing the water transmission resistance during filtration. Therefore, it is more economical by adding nanoparticles to organic phase than aqueous phase under the same filtering effect. On the other hand, different nanoparticles can also cause differences in performance and structure of the TFN membranes even in the same preparation manner. TFN membrane with UiO-66-NH2 in the aqueous phase has higher water permeance than the one with UiO-66 in the aqueous phase, owning to good hydrophilicity of amino group, which improves the water dispersibility of UiO-66-NH2, so that the TFN membrane is more uniform. In addition, UiO-66-NH2 slows down the process of interface polymerization, making the membrane more porous. The monomers in aqueous phase and the organic phase can be adsorbed in the pores of Zr-MOFs, which makes the interfacial polymerization occur both in the pores and on the surface of the pores. Thus, the compatibility between the polyamide and MOFs was enhanced and less defects was formed in the thin film layer, resulting in high salt rejection even the concentration of Zr-MOFs increased. This is the first time to explain that polyamide membrane has not obvious salt rejection attenuation with increasing porous material content using pore adsorption reaction monomer principle. Also, the Zr-MOFs based TFN membrane exhibited good heat resistance and anti-fouling property. This work shows that porous Zr-MOFs nanomaterials have significant advantages in the development of nanofiltration membranes with high water flux and rejection.

Recycling metal-organic framework residues (MOFRs) as bifunctional additives in fabricating porous ceramic membranes

Preparation and Modification of Ceramic Membrane and Its Application in Oil/Water Wastewater Treatment

Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.

Transformation of Metal-Organic Frameworks for Molecular Sieving Membranes

MOF-Enhanced Aluminosilicate Ceramic Membranes Using Non-Firing Processes for Pesticide Filtration and Phytochrome Removal

Metal based gels as versatile precursors to synthesize stiff and integrated MOF/polymer composite membranes

In Situ Assembly of Polyamide/Fe(BTC) Nanocomposite Reverse Osmosis Membrane Assisted by Fe3+-Polyphenolic Complex for Desalination

Zeolite Imidazolate Frameworks-8@SiO2-ZrO2 Crystal-Amorphous Hybrid Core-Shell Structure as a Building Block for Water Purification Membranes

Fe-Mn Bimetallic Oxide-Enabled Facile Cleaning of Microfiltration Ceramic Membranes for Effluent Organic Matter Fouling Mitigation via Activation of Oxone

Design and Construction of Ag@MOFs Immobilized PVDF Ultrafiltration Membranes with Anti-bacterial and Antifouling Properties

Asymmetric alumina-based ultrathin composite ceramic membranes with interfacial modification of black talc nanosheets

Freestanding Metal Organic Framework‐Based Multifunctional Membranes Fabricated via Pseudomorphic Replication toward Liquid‐ and Gas‐Hazards Abatement

Overcoming the Trade-off between Water Permeation and Mechanical Strength of Ceramic Membrane Supports by Interfacial Engineering

Enhanced water treatment performance of ceramic-based forward osmosis membranes via MOF interlayer

Anodized Aluminum Oxide Templated Synthesis of Metal–Organic Frameworks Used As Membrane Reactors

Fluorinated Strategy of Node Structure of Zr-based MOF for Construction of High-Performance Composite Polymer Electrolyte Membranes

Impacts of Metal-Organic Frameworks on Structure and Performance of Polyamide Thin-Film Nanocomposite Membranes.

Fabrication of PVDF@MOF-303 membrane with Mortise-Tenon structure by the polyphenol analogue-assisted growth strategy for oil-water separation and heavy metal adsorption

Porous Zr-based metal organic frameworks (Zr-MOFs) incorporated thin film nanocomposite membrane toward enhanced desalination performance.

Fabrication of water-stable MOF-808 membrane for efficient salt/dye separation

Enhancing Nanofiltration Selectivity of Metal-Organic Framework Membranes via a Confined Interfacial Polymerization Strategy