Abstract:<p>A circumferential crack in the fusion line is a major threat to the structural integrity of the pipeline girth weld because it may possibly lead to fracture failure when subjected to large plastic deformations. For the newly constructed X80 pipeline with an outside diameter (OD) of 1422 mm in China, the complicated configuration of welded joints and the outer diameter are outside the range of the general fracture assessment standards, such as BS 7910. Furthermore, during the pipe manufacture process, pipeline designers merely specify the minimum yield strength limit according to the pipe steel grade. This results in a wide variation range in the choice of yield strength values of the base metal. This also leads to a serious problem in the fracture assessment of pipe girth weld because the weld strength is commonly considered to be either evenly matched or overmatched. The foregoing factors make it difficult to perform an accurate fracture assessment using conventional standards. This study therefore aims to investigate the fracture behavior of 1422-mm OD pipelines with a double-V groove weld and circumferential crack in the fusion line. The specific effect of material mismatch and the realistic operational parameters that influence the fracture capacity of the pipe are examined via a series of numerical investigations. First, a rigorous three-dimensional finite element model to simulate the pipe girth weld is established by utilizing the ABAQUS finite element code package. The weld, which has a canoe-shaped surface crack in the fusion line between the heat-affected zone and root welding metal, is subjected to biaxial loading conditions. The keyhole method is adopted to simulate the crack front as well as the crack tip to eliminate the stress singularity effect during deformation. A refined mesh strategy is introduced to ensure the accurate simulation of the stress and strain fields in the vicinity of the crack tip. Based on the numerical model, the J-integral fracture parameter, which is clearly defined based on a strict mechanical theory, is chosen to characterize the effect of strength matching ratio, internal pressure, and yield to tensile strength ratio on the crack driving force. A new strain-based J-integral prediction formula is proposed based on numerical results.</p>

Effect of welding axial stresses on the strength of a welded pipe joint with a defect

Research On Safety Assessment Method For Pressure Pipe With Incomplete Welding Defects Under Complicated Loadings

Plastic Limit Load Analysis for Pressure Pipe with Incomplete Welding Defects Based on the Extended Net Section Collapse Criteria

Safety Test Research of Pressure Pipes Containing Incomplete Welding Defects

Role of welding residual stress in stainless steel piping with application of the leak-before-break technology

Surface Stress Analysis of Internally Corroded Pipes under External Pressure

Inhomogeneous Strain Behaviors of the High Strength Pipeline Girth Weld under Longitudinal Loading

Finite element analysis of the failure of high-strength steel pipelines containing group corrosion defects

Prediction of static failure in metal inert gas welded nuclear grade pipe 347 SS: Experimentation and finite-element analysis approach

The Effect of Pipeline Root Weld Microstructure on Crack Growth Behaviour

Stress–Strain Analysis of a Pipeline With Inner and Outer Corrosion Defects

The impact of residual technological stresses on the opening and stability of through cracks in pipeline elements

Stress Analysis of the Effect of Additional Load on the Butt Weld of Suspended Pipeline With Variable Wall Thickness

Effect of Yield Strength Distribution Welded Joint on Crack Propagation Path and Crack Mechanical Tip Field

Fracture response of 1422-mm diameter pipe with double-V groove weld joints and circumferential crack in fusion line

Research on Failure Pressure of API 5L X100 Pipeline with Single Defect

Modeling of mechano-electrochemical interaction at a corrosion defect on a suspended gas pipeline and the failure pressure prediction

Safety assessment of incomplete penetration defects at the root of girth welds in pipelines

Effect of Steel Properties on Buckling Pressure of Corroded Pipelines

Fracture behavior analysis of X80 pipelines welded joints with unequal wall thickness

Effects of Welding and Constraint Conditions on the Welding Residual Stress and Hardness of Type 316 Stainless Steel Pipe