Abstract:In recent years, to progress towards carbon emissions reduction, photovoltaic technology has become one of the most significant methods of generating electricity using renewable sources. However, the accumulation of ice and snow during the winter season affects the decrease in the power generation efficiency of photovoltaic modules. As a promising solution, coatings that exhibit anti-icing properties can be used. To date, no efficient ice-phobic coating has been developed for use on photovoltaic panels. In this paper development of transparent silicone-epoxy coatings modified with bi- and tri-functionalized octaspherosilicates was presented. The used organosilicone-based modifiers reveal both types of functional groups: one increases the surface properties and the second compatibility with the polymer matrix. The icephobic properties were discussed by determining an ice adhesion (IA) and a freezing delay time of water droplets (FDT). The coating exhibiting the highest anti-icing performance achieved the IA of 102 kPa and the FDT of 210 min, a 43 % reduction and a 70 times increase in value compared to the unmodified coating, respectively. The performed study included also the characterization of hydrophobic properties: water contact angle (WCA) at room temperature and below 0°C, contact angle hysteresis(CAH), and roll-off angle (RoA) as well as surface roughness and coatings thickness. In addition, the correlations between them and ice adhesion/freezing delay time were determined. It was found that roughness as well as dynamic parameters of the wettability of CAH and RoA have a significant effect on the obtained IA values. Moreover, the developed coatings can be potentially applied to photovoltaic panels, since the conducted modification did not affect the optical properties of the investigated coatings.

Anti-icing transparent coatings modified with bi- and tri-functional octaspherosilicates for photovoltaic panels