Mechanical properties and durability evaluation of self-compacting mortars containing glass and brick powders

Yasmina Bouleghebar,Mohamed Bentchikou,Otmane Boukendakdji

DOI: https://doi.org/10.54021/seesv5n2-032

2024-07-18

STUDIES IN ENGINEERING AND EXACT SCIENCES

Abstract:The present Paper examines the mechanical properties and some durability aspects of self-compacting mortars (SCM) with Glass (GP) and Brick Powders (BP) at different cement replacement levels, along with different finenesses. The mechanical properties that have been evaluated by compressive and flexural strength tests at the ages of 07, 14, 28, 56, 90 and 400 days, shrinkage tests, alkali-silica reaction (ASR), microstructure and high temperature strength tests of 90-day cured SCM, exposed to 400°C, 600°C and 800°C, have been conducted. The results indicated that SCM with Glass Powder (SCM-GP) and Brick Powder (SCM-BP) have showed an improvement in compressive and flexural strengths with increasing fineness, and alike with the curing age compared to the control SCM. Likewise, the drying shrinkage of SCM-GP has significantly reduced with the addition of GP, whilst the shrinkage increased for SCM-BP, with the increase of BP, but still remained lower or equal to the one relating to the control SCM. This study has alike showed that the expansion following the alkali-silica reaction for SCM-GP at 24% GP, and SCM-BP at 20% BP, was significantly lower than the control mixture; further, the reduction is 54% and 64% respectively compared to the control mixture. But also, the SCM with GP and BP showed better performance in terms of high temperature resistance. This study brings to light the possibility of producing ecological cementitious composites from waste glass and calcined brick, as a partial replacement for Portland cement.