Abstract:In order to analyze and predict the corrosion ratio and rust layer distribution of steel rebar embedded in reinforced concrete under time-varying climatic conditions, a self-balancing steel corrosion model was established by connecting the environmental temperature, humidity, external chloride ions and oxygen concentration to the potential distribution and current density of the steel using finite element method. The model covered the whole corrosion process of steel rebar in concrete under natural climate, including the steel rebar depassivation, steel corrosion propagation and the rust layer expansion on the surface of steel rebar. In the proposed model, the microcell and macrocell corrosion were coupled by electrochemical polarization, and the cathode-to-anode area ratio was determined by the time-varying chloride distribution at the rebar surface. Taking the diffusion of chloride ions and oxygen in concrete into account, the distribution of corrosion potential of reinforcement, the change of corrosion current density of reinforcement, and the distribution of rust layer on the surface of reinforcement can be obtained based on the variation of natural temperature and humidity. The proposed model was validated utilizing the experimental data from the literatures. On this basis, a discussion about the influence of long-term climatic environments on the corrosion kinetics were conducted. The results suggest that environmental temperature and relative humidity affect the steel corrosion process mainly by affactting the chloride and oxygen diffusion coefficients, concrete resistivity, and concentration of dissolved oxygen in concrete pore solution. The corrosion current density of steel in concrete is sensitively influenced by the environmental temperature more than relative humidity. Although the initial exposure time has a significant impact on the accumulation process of chloride on steel surface within one climatic cycle, it has little influence on the final chloride distribution at the end of the period. However, the initial exposure time remarkably influences the evolution profile of rust layer thickness during the climatic cycle. The steel rebar initially exposed to a higher temperature suffers from more severe corrosion than that initially exposed to a lower temperature.

Research on accelerated corrosion of 0Cr18Ni9 stainless steel in marine atmospheric environment of the South China Sea

Study on the Correlation Between Indoor Accelerated Corrosion Testing of Concrete Epoxy Polysiloxane Coating and Real-Sea Environmental Testing in the East China Sea

Correlation between Laboratory-Accelerated Corrosion and Field Exposure Test for High-Strength Stainless Steels

Study on corrosion behavior and mechanism of AISI 4135 steel in marine environments based on field exposure experiment

Corrosion behavior research and corrosion prediction of structural steel in marine engineering

Study on corrosion behavior of typical carbon steel and low alloy steel in deep sea of different sea areas

Research on Atmospheric Corrosion of 45# Steel in Low-Latitude Coastal Areas of China

Corrosion of Steel Embedded in Mortar and Concrete under Different Electrolytic Accelerated Corrosion Methods

A Comparative Study of the Corrosion Behavior of 30CrMnSiNi2A in Artificial Seawater and Salt Spray Environments

SIMULATED RESEARCH ON CORROSION OF REINFORCEMENT IN CONCRETE UNDER CHLORIDE ENVIRONMENT

Numerical simulation of electrochemical mechanism of steel rebar corrosion in concrete under natural climate with time-varying temperature and humidity

Dynamic Self-Balanced Electrochemical Model for Non-Uniform Corrosion of Steel Reinforcement in Concrete under Combined Effects of Heat-Moisture-chlorine-oxygen

Multi-performance evaluation of high-throughput accelerated corrosion test for high-strength low-alloy 921A steel

Accelerating Tests For The Performance Deterioration Of Concrete Exposed To Chloride Media

Investigation of Microstructure and Corrosion Behavior of Weathering Steel in Aqueous Solution Containing Different Anions for Simulating Service Environments

Numerical Simulation of Steel Corrosion in Chloride Contaminated Concrete

Pitting corrosion of 2Cr13 stainless steel in deep-sea environment

A Method for Predicting the Corrosion Behavior of Structural Steel under Atmosphere

A study on corrosion behavior of advanced weathering steel relying on Ni-Mo synergy under marine atmosphere

Corrosion behavior of the low alloy weathering steels coupled with stainless steel in simulated open atmosphere

Study of corrosion and failure mechanism of the galvanized steel pipes of meteorological tower serviced in the South China Sea