A robust and highly active bimetallic phosphide/oxide heterostructure electrocatalyst for efficient industrial-scale hydrogen production
Balakrishnan Kirubasankar,Jisu Kwon,Sohyeon Hong,Yo Seob Won,Soo Ho Choi,Jeeho Lee,Jae Woo Kim,Ki Kang Kim,Soo Min Kim
DOI: https://doi.org/10.1016/j.nanoen.2024.109805
IF: 17.6
2024-06-10
Nano Energy
Abstract:Efficient and durable high-current-density bifunctional electrocatalysts are vital for cost-effective production of alkaline water electrolyzers (AWEs) on an industrial scale. However, existing commercial catalysts, such as Raney Ni which requires over 2.5 V for just 500 mA cm −2 , fail to achieve high current densities with low cell voltages. In this study, we introduce a bifunctional RuP 2 /Ni 5 P 4 /NiMoO 4 heterostructure electrocatalyst, synthesized via a facile hydrothermal method, followed by the controlled addition of ruthenium (Ru) and subsequent phosphorization. This process yielded (Ru, Ni) phosphides and NiMoO 4 with a moderate weight percentage and mass loading of Ru content, approximately 1.02 wt% and 61 μg cm −2 , respectively. The synergistic effect of these phosphides and bimetallic oxides significantly improves water dissociation, as well as the hydrogen and oxygen evolution reaction (HER and OER) performances. Under industrial conditions (80 °C and 6 M KOH), our catalyst achieves low overpotentials of 273 mV for HER and 390 mV for OER at 2000 mA cm −2 , outperforming commercial Pt/C and RuO 2 catalysts. Additionally, in an AWE, our catalyst maintains a low operating voltage of 1.76 V for 1 A cm −2 , with consistent performance over 100 h at 500 mA cm −2 . It records an electricity consumption of 3.97 kW h Nm − 3 and an electrolyzer efficiency of 89.1%, underscoring its potential for cost-effective industrial applications. Furthermore, accelerated degradation tests under variable current loads show no significant change in cell voltage and high-frequency resistance (HFR), demonstrating robustness for intermittent energy sources. This work proposes a novel design principle for high-performance electrocatalysts, significantly reducing reliance on noble metals and offering a robust, efficient solution for industrial-scale hydrogen production.
materials science, multidisciplinary,nanoscience & nanotechnology,physics, applied,chemistry, physical