Manipulating d‐Band Center of Ru Sites in Branched RuO2 Nanofibers Enables Significantly Enhanced Alkaline Overall Water Splitting Performance

Linfeng Zhang,Weimo Li,Siyu Ren,Wei Song,Ce Wang,Xiaofeng Lu

DOI: https://doi.org/10.1002/aenm.202403136

IF: 27.8

2024-10-11

Advanced Energy Materials

Abstract:Branched phosphorus (P)‐doped ruthenium dioxide (RuO2) nanofibers are constructed to manipulate the d‐band center of ruthenium sites and optimize the adsorption/desorption energy of reaction intermediates during hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) processes. Thus the obtained P‐doped RuO2 nanofibers present outstanding alkaline industrial‐grade‐current‐density HER and OER performance, enabling an overall water‐splitting application. Although ruthenium dioxide (RuO2) is an efficacious oxygen evolution reaction (OER) catalyst in acidic media, its performance in alkaline conditions is subpar and it is also ineffective for hydrogen evolution reaction (HER) in common electrolytes. Here, an effective phosphorus (P)‐doping strategy is introduced to manipulate the d‐band center of ruthenium (Ru) sites, attenuating the adsorption energy of HER intermediates and lowering the energy barrier in OER, thereby significantly accelerating both HER and OER performance. The representative 10%P‐RuO2 nanofibers (NFs) catalyst presents an ultralow overpotential of 177.9 mV at 1 A cm−2 and long‐term stability of 300 h in 1 m KOH toward HER, greatly exceeding those of benchmark platinum (Pt)/C catalyst. Moreover, the 10%P‐RuO2 NFs catalyst exhibits an exceptional OER performance with a low overpotential of 250 mV at 10 mA cm−2 (η10) and desirable stability of 150 h at 1 A cm−2, which is far better than commercial RuO2 and many other typical previously reported OER catalysts. Additionally, an overall water electrolytic cell using 10%P‐RuO2 NFs as both anode and cathode necessitates a working voltage of 1.52 V (η10) and demonstrates long‐term stability over 100 h at 1 A cm−2, outperforming many typical water electrolysis cells.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,energy & fuels