Abstract:Low elongation has been an important factor limiting the application of titanium/304 stainless steel (304SS) laser welding of dissimilar metal joint products. By adopting the post-weld heat treatment (PWHT) process of holding the welded joint at 400 °C, 550 °C and 700 °C for 30 min, this study increases the elongation of the welded joint from 0.3 % to 2.21 % in the welded state and further analyses and investigates the structural changes in the organization and the formation process of intermetallic compounds (IMC) within the weld seam. The results showed that the acicular structure in the weld could not be eliminated by holding at 400 °C for 30 min, but only part of the residual stress was released, and the elongation was increased to 0.85 %. After holding at 550 °C for 30 min, a large number of equiaxed crystals appeared to replace the acicular structure in the weld and released the residual stress. With the enhancement of the IMC layer thickness, grain gap and deformation coordination ability, the elongation increased to 2.21 %. After holding at 700 °C for half an hour, the IMC layer becomes thinner, the grain gap decreases, the deformation coordination ability deteriorates, and the tensile strength and elongation decrease. In the tensile test, the fracture position was all at the weld. After being held at 400 °C for 30 min, the average tensile strength of the tensile sample increased from 330 MPa in the welded state to 352 MPa; after being held at 550 °C for 30 min, the average tensile strength of the tensile sample was 340 MPa, and the fracture elongation was 7.4 times that of the welded state, reaching 331 μm.

Enhanced strength of laser welded steel/titanium butt joints with vanadium multi-layers and a copper plate as a composite intermediate layer

Dissimilar Joining of TC4 Alloys to 304 Stainless Steels Using a Novel V/CuCrZr Composite Interlayer

Single-pass laser welding of TC4 Ti alloy to 304 SS with V interlayer and V/Cu bilayer

Microstructure and mechanical properties of laser welded titanium alloy and stainless steel joint with composite interlayer

Fabrication of highly dissimilar TC4/steel joint with V/Cu composite transition layer by laser melting deposition

Microstructure and Mechanical Property Improvement in Laser-Welded TC4 Titanium Alloy and 301L Stainless Steel Joints Without Filler Metal

Microstructure, Variant Selection, and Mechanical Properties of Laser-Welded Ti-4Al-2V Joints

Experimental and numerical study on microstructure and mechanical properties for laser welding-brazing of TC4 Titanium alloy and 304 stainless steel with Cu-base filler metal

Effect of Vanadium Layer on Microstructure and Properties of TC4 (Ti-6Al-4V)/TiAl (Ti-48Al-2Cr-2Nb) Dissimilar Metals Produced by Laser Additive Manufacturing

Double-pass laser welding of TC4 alloy and 304 stainless steel

Single-pass laser brazing of TC4 alloy and 304 stainless steel with Cu interlayer and Cu-Zn filler metal

Microstructure and mechanical property improvement of Ti alloy and stainless steel joint based on a hybrid connection mechanism

Microstructure and Mechanical Properties of Dissimilar TC4 Titanium Alloy/304 Stainless Steel Joint Using Copper Filler Wire

Effect of post-weld heat treatment on the microstructure and properties of titanium/304 stainless steel laser welding dissimilar metal joints with copper as the transition layer

Microstructure and Impact Toughness of Laser-Arc Hybrid Welded Joint of Medium-Thick TC4 Titanium Alloy

Study of the Microstructure and Properties of the Butt Joint of Laser-Welded Titanium Alloy with Flux-Cored Wire

Diffusion Welding for TC4 Titanium Alloy/T2 Copper with Vanadium Foil

Microstructure and Mechanical Properties of Arc Zone and Laser Zone of TC4 Titanium Alloy Laser–TIG Hybrid Welded Joint

Improving bonding strength and reliability of brazed titanium/copper dissimilar joint using vanadium interlayer

Integrated laser additive manufacturing of high-strength steel and Ti6Al4V: Experimental investigations and thermodynamic calculations

Investigation of strengthening mechanism of commercially pure titanium joints fabricated by autogenously laser beam welding and laser-MIG hybrid welding processes