Abstract:The catalytic conversion of dinitrogen (N-2) into ammonia under ambient conditions represents one of the Holy Grails in sustainable chemistry. As a potential alternative to the Haber-Bosch process, the electrochemical reduction of N-2 to NH3 is attractive owing to its renewability and flexibility, as well as its sustainability for producing and storing value-added chemicals from the abundant feedstock of water and nitrogen on earth. However, owing to the kinetically complex and energetically challenging N-2 reduction reaction (NRR) process, NRR electrocatalysts with high catalytic activity and high selectivity are rare. In this contribution, as a proof-of-concept, we demonstrate that both the NH3 yield and faradaic efficiency (FE) under ambient conditions can be improved by modification of the hematite nanostructure surface. Introducing more oxygen vacancies to the hematite surface renders an improved performance in NRR, which leads to an average NH3 production rate of 0.46 mu g h(-1) cm(-2) and an NH3 FE of 6.04 % at -0.9 V vs. Ag/AgCl in 0.10 m KOH electrolyte. The durability of the electrochemical system was also investigated. A surprisingly high average NH3 production rate of 1.45 mu g h(-1) cm(-2) and a NH3 FE of 8.28 % were achieved after the first 1 h chronoamperometry test. This is among the highest FEs reported so far for non-precious-metal catalysts that use a polymer-electrolyte-membrane cell and is much higher than the FE of precious-metal catalysts (e.g., Ru/C) under comparable reaction conditions. However, the NH3 yield and the FE dropped to 0.29 mu g h(-1) cm(-2) and 2.74 %, respectively, after 16 h of chronoamperometry tests, which indicates poor durability of the system. Our results demonstrate the important role that the surface states of transition-metal oxides have in promoting electrocatalytic NRR under ambient conditions. This work may spur interest towards the rational design of electrocatalysts as well as electrochemical systems for NRR, with emphasis on the issue of stability.

Highly selective electrochemical reduction of nitrate-to-ammonia using iron phosphide self-supported electrode

Highly active iron phosphide catalysts for selective electrochemical nitrate reduction to ammonia

Phosphorization of α‐Fe2O3 Boosts Active Hydrogen Mediated Electrochemical Nitrate Reduction to Ammonia

Selective Electrocatalytic Reduction of Nitrate to Ammonia with Nickel Phosphide.

Fe3O4 nanoparticle-decorated 3D pinewood-derived carbon for high-efficiency electrochemical nitrate reduction to ammonia

High-Performance Electrochemical Nitrate Reduction to Ammonia under Ambient Conditions Using a FeOOH Nanorod Catalyst

Ultralow overpotential 465 mV: Ni and Fe synergistically promote the conversion of nitrate to ammonia

Iron and Nickel Based Alloy Nanoparticles Anchored on Phosphorus-Modified Carbon-Nitrogen Plane Enhances Electrochemical Nitrate Reduction to Ammonia

Self-supported P-doped NiFe 2 O 4 micro-sheet arrays for the efficient conversion of nitrite to ammonia

Cu-Doped Iron Oxide for the Efficient Electrocatalytic Nitrate Reduction Reaction.

Ambient Electrochemical N 2 Reduction to NH 3 on Nitrogen and Phosphorus Co‐doped Porous Carbon with Trace Iron in Alkaline Electrolytes

Highly Selective Electrochemical Reduction Of Dinitrogen To Ammonia At Ambient Temperature And Pressure Over Iron Oxide Catalysts

Enhanced Metal–Support Interfacial Interaction of Pd@FeNi-CoO Composites for Efficient Nitrate Reduction to Ammonia

Breaking Local Charge Symmetry of Iron Single Atoms for Efficient Electrocatalytic Nitrate Reduction to Ammonia.

High-Performance Electrocatalytic Reduction of Nitrite to Ammonia under Ambient Conditions on a FeP@TiO<sub>2</sub> Nanoribbon Array

Electrodeposited NiCoP on nickel foam as a self-supported cathode for highly selective electrochemical reduction of nitrate to ammonia

Efficient Ammonia Electrosynthesis and Energy Conversion through a Zn‐Nitrate Battery by Iron Doping Engineered Nickel Phosphide Catalyst

Self‐Supported Pd Nanorod Arrays for High‐Efficient Nitrate Electroreduction to Ammonia

Fe Nanoparticles Decorated Pinewood‐Derived Carbon for Highly Efficient Electrocatalytic Conversion of Nitrite to Ammonia

Ambient Ammonia Synthesis via Nitrate Electroreduction in Neutral Media on Fe<sub>3</sub>O<sub>4</sub> Nanoparticles-decorated TiO<sub>2</sub> Nanoribbon Array

A Bioinspired Iron-Centered Electrocatalyst for Selective Catalytic Reduction of Nitrate to Ammonia