An Ultrahigh Rate and Stable Zinc Anode by Facet‐matching‐induced Dendrite Regulation
Zhehan Yi,Jiaxin Liu,Shandong Tan,Zhiyuan Sang,Jing Mao,Lichang Yin,Xiaoguang Liu,Liqun Wang,Feng Hou,Shi Xue Dou,Hui‐Ming Cheng,Ji Liang
DOI: https://doi.org/10.1002/adma.202203835
IF: 29.4
2022-07-31
Advanced Materials
Abstract:Resource‐abundant metal (e.g., zinc) batteries feature intrinsic advantages of safety and sustainability. Their practical feasibility, however, is impeded by the poor reversibility of metal anode, typically caused by the uncontrollable dendrite enlargement. Significant effort has been exerted to completely prevent dendrites from forming, but this seems less effective at high current densities. Herein, we present an alternative dendrite regulation strategy of forming tiny, homogeneously distributed, and identical zinc dendrites by facet matching, which effectively avoids undesirable dendrite enlargement. Confirmed by multiscale theoretical screening and characterization, the regularly exposed Cu(111) facets at the ridges of a copper nanowire are capable of such dendrite regulation by forming a low‐mismatched Zn(002)/Cu(111) interface. Consequently, reversible zinc electroplating/stripping has been achieved at an unprecedentedly high rate of 100 mA cm−2 for over 30,000 cycles, corresponding to an accumulative areal capacity up to 30 Ah cm−2. A full cell using this anode shows a high capacity of 308.3 mAh g−1 and a high capacity retention of 91.4% after 800 cycles. This strategy is also viable for magnesium and aluminum anodes, thus opening up a promising and universal avenue towards long life and high rate metal anodes. This article is protected by copyright. All rights reserved
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology