Preparation and characterization of ferrous oxalate cement—A novel acid‐base cement

Zhongqiu Luo,Yue Ma,Huan He,Weihong Mu,Xintao Zhou,Wenyu Liao,Hongyan Ma

DOI: https://doi.org/10.1111/jace.17511

IF: 4.186

2020-10-21

Journal of the American Ceramic Society

Abstract:<p>Ferrous oxalate cement (FOC), a new type of acid‐base cement, is prepared at room temperature through reactions between iron‐rich copper slag (CS) and oxalic acid (OA). In this work, the influences of precursor proportions, including the copper slag‐to‐oxalic acid mass ratio (CS/OA), borax‐to‐cement mass ratio (B/C) and water‐to‐cement mass ratio (W/C), on the setting behaviour and compressive strength of FOC paste are investigated. Furthermore, the evolutions of pH and ions concentrations are traced to understand the reaction mechanism of FOC. The results show that the compressive strength decreases with an increase in W/C; when W/C is fixed, with an increase in CS/OA, the compressive strength first increases and then decreases, giving an optimal value. The compressive strengths of specimens at 3, 7 and 28 d can reach 33, 41 and 55 MPa, respectively, under the optimal conditions (CS/OA = 3.6, B/C = 0.03 and W/C = 0.18). The setting time is also a function of W/C and CS/OA, and can be extended by adding borax. Iron oxalate hydrate (FeC₂O₄·2H₂O) has been identified as the exclusive hydration product of FOC due to the chemical reaction between Fe₂SiO₄ or Fe₃O₄ contained in CS and OA solution. At the initial stage of reaction, OA is dissolved to release protons, HC₂O₄⁻ and C₂O₄²⁻, which facilitate the dissolution of Fe₂SiO₄ and Fe₃O₄ and the release of Fe²⁺ in the aqueous phase. Then the Fe²⁺ ions combine with HC₂O₄⁻ and C₂O₄²⁻ to precipitate FeC₂O₄·2H₂O, acting as the cementitious phase to bond the unreacted CS particles.</p>

materials science, ceramics