Abstract:This present study mainly focuses on the influence of low-calcium circulating fluidized bed fly ash (LCFA) on the mechanical property and microstructure of cement-based materials under different curing conditions. The mechanical properties test was conducted by changing variable parameters, such as LCFA content, the internal mixing ratio of LCFA and fly ash (FA), and dry and water curing conditions. Further, the hydration products and pore structure were analyzed using XRD, FT-IR, TG-DTG, NI, SEM, and BET micro-testing technology. The strength development law of LCFA on cement-based materials is discussed. The research results show that LCFA has a certain degree of self-hardening and can be used as a cementitious material in cement-based materials. Still, the loose and porous microstructure of LCFA leads to higher water requirements, which reduces the fluidity of cement-based pastes. Water curing is favorable for promoting the development of LCFA on the long-term compressive strength of cement-based materials. When the LCFA was added to the cement, the optimal substitution ratio was 20%, and the compressive strength at 91 days reached 101 MPa. In the case of compounding LCFA and FA, when the internal mixing ratio of LCFA/FA was 3 and the total content was 20%, the mechanical properties were the highest, and the compressive strength at 91 days was 92 MPa. The microscopic analysis result shows that the cumulative hydration heat of the samples decreased significantly with the increase of dosage of LCFA. The main hydration products of cement-based materials mixed with LCFA were AFt, C-S-H gel, and Ca(OH)2. AFt and C-S-H gels are critical to the strength development of OPC-LCFA samples. The active Al2O3 and active SiO2 in LCFA were involved in hydration reactions to promote the formation of C-A-H and C-S-H gel and effectively promote the development of the mechanical properties. Overdosages of LCFA would reduce the ettringite formation rate. FA is not conducive to AFt formation in the hydration process of OPC-FA samples.

Effects of calcium formate on early-age strength and microstructure of high-volume fly ash cement systems

Effect of calcium formate on the compressive strength, and hydration process of cement composite containing fly ash and slag

Microstructural Investigation of High-Volume Fly Ash Composites Containing Nano-Calcium Silicate Hydrate Crystals

Microstructure and Strength Development of Quaternary Blend High-Volume Fly Ash Concrete

Investigation of Low-Calcium Circulating Fluidized Bed Fly Ash on the Mechanical Strength and Microstructure of Cement-Based Material

From Hydration to Strength Properties of Fly Ash Based Mortar

Strength and Microstructural Characteristics of Activated Fly Ash–Cement Paste

Hydration and Strength Evolution of Ternary-Blend High-Volume Fly Ash Concretes

Effect of Sulfate Activators on Mechanical Property of High Replacement Low-Calcium Ultrafine Fly Ash Blended Cement Paste

Effect of Composite Fibers and Fly Ash on the Properties of Portland–Sulfoaluminate Composite Cement-Based Grouting Sealing Materials

Effect of calcium formate as an accelerator on the physicochemical and mechanical properties of pozzolanic cement pastes

Enhancement of compressive strength of high-volume fly ash cement paste by wet grinded cement: Towards low carbon cementitious materials

Influence Mechanisms of Fly Ash in Magnesium Ammonium Phosphate Cement

Molecular mechanism of fly ash affecting the performance of cemented backfill material

The cation-dependent effects of formate salt additives on the strength and microstructure of CaO-activated fly ash binders

The role of fly ash microsphere in the microstructure and macroscopic properties of high-strength concrete

Effects of Fly Ash Particle Size and Chemical Activators on the Hydration of High-Volume Fly Ash Mortars

The Early Age Strength Improvement of the High Volume Fly Ash Mortar

The Effects of Hardening Accelerator on Microstructure and Mechanical Performance of Fly-Ash Cement-Based Materials Using Response Surface Methodology

Influence of fly ash on mechanical properties and hydration of calcium sulfoaluminate-activated supersulfated cement

Nano-CSH Modified High Volume Fly Ash Concrete: Early-age Properties and Environmental Impact Analysis